A Spinel Tin Ferrite with High Lattice-Oxygen Anchored on Graphene-like Porous Carbon Networks for Lithium-Ion Batteries with Super Cycle Stability and Ultra-fast Rate Performances
Chao-Feng Pan,Yan-Hui Sun,Chen-Hao Sun,Zi-Yu Wang,Jun-Min Nan
DOI: https://doi.org/10.1021/acsami.2c00321
2022-04-13
Abstract:A new type of nano-SnFe2O4 with stable lattice-oxygen and abundant surface defects anchored on ultra-thin graphene-like porous carbon networks () is prepared for the first time by an interesting freezing crystallization salt template method. The functional composite has excellent rate performance and long-term cycle stability for lithium-ion battery (LIB) anodes due to the stable structure, improved conductivity, and shortened migrating distance for lithium-ions, which are derived from the higher lattice-oxygen of SnFe2O4, abundant porous carbon networks and surface defects, and smaller nanoparticles. Under the ultra-high current density of 10, 15, and 20 A g–1 cycling for 1000 times, the can provide high reversible capacities of 522.2, 362.5, and 361.1 mAh g–1, respectively. The lithium-ion storage mechanism of the composite was systematically studied for the first time by in situ X-ray diffraction (XRD), ex situ XRD and scanning electron microscopy (SEM), and density functional theory (DFT) calculations. The results indicate that the existence of Li2O and metallic Fe during the lithiation/delithiation process is a key reason for reducing the initial lithium-ion storage reversibility but increasing the rate performance and capacity stability in the subsequent cycles. DFT calculations show that lithium-ions are more easily adsorbed on the (111) crystal plane with a much lower adsorption energy of −7.61 eV than other planes, and the Fe element is the main acceptor of electrons. Moreover, the kinetics investigation indicates that the lithium-ion intercalation and deintercalation in are mainly controlled by the pseudocapacitance behavior, which is favorable to enhancing the rate performance. The research provides a new strategy for designing LIB electrode materials with a stable structure and outstanding lithium-ion storage performance.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c00321.SEM images of the prepared samples at different magnifications (Figure S1); SEM images and XRD of (Figure S2); SEM images of the precursor of the samples calcined at 600 °C before washing (Figure S3); TEM images of carbon layers for the samples (Figure S4); TEM images and elemental mapping of (Figure S5); the XRD patterns and SEM morphology of the precursor at different annealing temperatures (Figures S6 and S7); XPS survey spectra of the samples (Figure S8); XPS spectra of Sn 3d, C 1s, and Fe 2p of SFO, , , and (Figures S9–S11); Raman spectra and the enlarged part of the wave number between 800 and 1000 cm–1 (Figure S12); UV–vis spectra of , , and (Figure S13); BET surface area and the pore size distribution profile of composites (Figure S14); the CV curves at 0.1 mV s–1, the charge–discharge curves, and the CV curves at different scan rates of SFO, , , and (Figures S15–S17); the pseudocapacitance contribution at different CV scan rates of the samples (Figure S18–S24); characterization of anodes cycled at the current density of 6A g–1 for and (Figure S25 for SEM and TEM images; Figure S26 for the cross-sectional SEM images); the initial cell structure of (a) and (b) (Figure S27); the PDOS diagram of s, p, and d atomic orbitals and the total contribution of (111) surface atoms of SnFe2O4 before and after lithiation (Figures S28 and S29); the detailed amount of the reagents used to prepare each sample (Table S1); the XRD peaks' intensity ratio of the obtained samples (Table S2); the integral area values of simulated O 1s peaks at different states (Table S3); the integral area values of D and G peaks of composites (Table S4); and the DFT calculation results of each crystal surface energy before and after the adsorption of lithium-ions (Table S5) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology