Removal of Heavy Metals Using a Novel Sulfidogenic AMD Treatment System with Sulfur Reduction: Configuration, Performance, Critical Parameters and Economic Analysis.

Rongrong Sun,Yu Li,Nini Lin,Chunxi Ou,Xiaoyi Wang,Liang Zhang,Feng Jiang

DOI: https://doi.org/10.1016/j.envint.2019.105457

IF: 11.8

2020-01-01

Environment International

Abstract:A novel sulfidogenic acid mine drainage (AMD) treatment system with a sulfur reduction process was developed. During the 220-d operation, > 99.9% of 380-mg/L ferric, 150-mg/L aluminum, 110-mg/L zinc, 20-mg/L copper and 2.5-mg/L lead ions, and 42.6-44.4% of 100-mg/L manganese ions in the synthetic AMD were step-by-step removed in the developed system with three pre-posed metal precipitators and a sulfur reduction reactor. Among them, zinc, copper and lead ions were removed by the biogenic hydrogen sulfide that produced through elemental sulfur reduction; while ferric, aluminum and manganese ions were removed by the alkali precipitation. Compared with the reported sulfate reduction reactors, the sulfur reduction reactor significantly reduced the chemical cost by 25.6-78.9% for sulfide production, and maintained a high sulfide production rate (1.12 g S2-/L-d). The pH level in the sulfidogenic reactor driven by sulfur-reducing bacteria posed a significant effect on the sulfide production rate. Under a nearly neutral condition (pH 7.0-7.5), elemental sulfur dissolved into polysulfide to increase the bioavailability of S-0. At acidic conditions (pH < 6.0), polysulfide formation was limited and sulfate reduction became dominant. Therefore, maintaining the sulfidogenic reactor driven by sulfur-reducing bacteria at neutral condition is essential to realize high-rate and low-cost AMD treatment. Moreover, the escape of residual hydrogen sulfide from the system was eliminated by employing a 17% recirculation from effluent to the sulfidogenic reactor.