Effects of the γ″-Ni 3 Nb Phase on Mechanical Properties of Inconel 718 Superalloys with Different Heat Treatments.

Li-Shi-Bao Ling,Zheng Yin,Zhi Hu,Jin-Hui Liang,Zhi-Yong Wang,Jun Wang,Bao-De Sun
DOI: https://doi.org/10.3390/ma13010151
IF: 3.4
2020-01-01
Materials
Abstract:The effects of the gamma "-Ni3Nb phase on the mechanical properties of Inconel 718 superalloys, with standard heat treatment, hot isostatic pressing + solution treatment + aging, and hot isostatic pressing + direct aging, were characterized by morphological observation, X-ray diffraction, and tensile experiments. The results of the morphological observation revealed that many fine gamma " precipitates of similar to 26.49 +/- 1.82 nm in mean size were formed in all samples. However, the relatively coarser gamma " precipitates formed in the grain boundaries were only observed in the sample treated with hot isostatic pressing + direct aging. The yield strengths of the hot isostatic pressing + direct aging sample at room temperature and at 650 degrees C both exhibited the maximum values about 993 +/- 5.7 and 811 +/- 12.6 MPa, respectively. The gamma " precipitate was considered to be the dominant strengthening phase in the sample according to the lattice misfits (epsilon) of gamma/gamma ". The strengthening mechanism of the samples can be explained as the coherency strain strengthening of fine gamma " precipitates. Moreover, due to the coarser gamma " precipitates in the grain boundaries, dislocation-cut ordered particle strengthening also occurred in the sample after hot isostatic pressing + direct aging treatment.
What problem does this paper attempt to address?