Abstract:The use of calcium oxide as a precipitant can achieve a nonammonia enrichment of a rare earth leaching liquor. However, an alkaline rare earth sulfate forms during the precipitation process, thus resulting in excessive SO42– content in the mixed rare earth oxides. Therefore, a stirring washing process for precipitation enrichment, which was obtained from calcium oxide precipitation, was investigated using a sodium hydroxide solution. It was determined that the Gibbs free energy of the stirring washing reaction, which was calculated by a group contribution method, was between −60 and −300 kJ/mol, depending on the different rare earth elements. The above results indicated that the reaction was thermodynamically feasible. The optimum conditions of the washing process were obtained, namely, a feed ratio of 2.85, a liquid–solid ratio of 6.5 mL/g, a stirring washing temperature of 35 °C, and a stirring washing time of 20 min. Under the optimal conditions, the purity and the SO42– content of the mixed rare earth oxides were 94.38% and 3.48%, respectively, and the stirring washing process with the sodium hydroxide solution had good recyclability. Moreover, the washing product was tested using thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffraction (XRD), and scanning electron microscopy-energy-dispersive spectrometry (SEM-EDS), which verified that the stirring washing process with NaOH could effectively remove SO42– from the precipitation enrichment into solution. On this basis, a new extraction process of the ion-adsorption-type rare earth ore by magnesium salt leaching–calcium oxide precipitation–sodium hydroxide stirring washing is proposed. This new process can eliminate the traditional aluminum-removal process and effectively reduces the rare earth loss in the process. It can also solve the problem of the excessive SO42– content in the mixed rare earth oxides caused by the calcium oxide precipitation process. The research in this paper can have great significance for green, efficient extraction of the ion-adsorption-type rare earth ore and the improvement of resource utilization.This article has not yet been cited by other publications.

Removal of Aluminum from Rare-Earth Leaching Solutions Via a Complexation-Precipitation Process

Separation of Rare Earth and Aluminum by Selective Complexation

Removal of Aluminum from Synthetic Rare Earth Leach Solution by Selective Complexation and Turbidity Point Extraction

A novel electrochemical method for the removal of aluminum from ionic rare earth leachate

Study on Aluminum Removal Through 5-Sulfosalicylic Acid Targeting Complexing and D290 Resin Adsorption

Reducing rare earth loss by adding acetic acid in the aluminum removal process of rare earth leaching solution

Removal of Sulfate Ions from Calcium Oxide Precipitation Enrichment of a Rare Earth Leaching Liquor by Stirring Washing with Sodium Hydroxide

Insight into leaching of rare earth and aluminum from ion adsorption type rare earth ore: Adsorption and desorption

Selective separation of rare earths and aluminum from low-concentration rare earth solution via centrifugal extraction

Separation of aluminum from rare earth by solvent extraction with 4-octyloxybenzoic acid

Leaching Mechanism of Aluminum during Column Leaching of Ion-Adsorption Rare Earth Ore Using Magnesium Sulfate

Study on the Effect and Mechanism of Impurity Aluminum on the Solvent Extraction of Rare Earth Elements (Nd, Pr, La) by P204-P350 in Chloride Solution

Leaching of rare earths and aluminum in weathered crust elution-deposited rare earth ore using magnesium sulfate: Effect of aluminum content in the leaching agent solution

The enrichment of rare earth from magnesium salt leaching solution of ion-adsorbed type deposit: A waste-free process for removing impurities

Partitioning behavior and mechanisms of rare earth elements during precipitation in acid mine drainage

Selective Recovery of Low-Concentration Light Rare Earth Ions from High-Concentration Ammonium Sulfate System by Coordination Ability

Novel Technology for the Removal of Fe and Al from Spent Li-Ion Battery Leaching Solutions by a Precipitation–Complexation Process

Electrodeposition of aluminum on rare earth alloy surface in room temperature molten salts

An eco-friendly and high-yield extraction of rare earth from the leaching solution of ion adsorbed minerals

Separation of Aluminum and Iron from Lanthanum—A Comparative Study of Solvent Extraction and Hydrolysis-Precipitation

Stepwise extraction of lithium and potassium and recovery of fluoride from aluminum electrolyte wastes through calcification roasting-two-stage leaching