Abstract:This study shows that in an atmosphere containing water vapor, the oxide layer on the surface of the 9CrNB steel MarBN (Martensitic 9Cr steel strengthened by Boron and MX Nitrides) was formed by an outer layer of hematite Fe2O3 and Cr2O3 and an inner two-phase layer of Fe3O4 and Fe3O4 + (Fe, Cr)2O4, which was confirmed by XRD analysis. Part of the layer consisted of nodules and pores that were formed during the increase in oxides when the present H2O(g) acted on the steel surface. The diffusion mechanism at temperatures of 600 and 650 °C and at longer oxidation times supported the “healing process” with a growing layer of Fe oxides and the presence of Cr and minor alloying elements. The effects of alloying elements were quantified using a concentration profile of the oxide layer based on quantitative SEM analysis, as well as an explanation of the mechanism influencing the structure and chemical composition of the oxide layer and the steel-matrix–oxide interface. In addition to Cr, for which the content reached the requirement of exceeding 7.0 wt. % in the inner oxide layer, W, Co, Mn, and Si were also found in increased concentrations, whether in the form of the present Fe-Cr spinel oxide or as part of a continuously distributed layer of Mn2O3 and SiO2 oxides at the steel-matrix–oxide interface. After long-term high-temperature oxidation, coarser carbides of the M23C6 type (M = Fe,W) significantly depleted in Cr were formed at the oxide-layer/matrix interface. In the zone under the oxide layer, very fine particles of MC (M = V, Nb, and to a lesser extent also Cr in the particle lattice of the given phase) were observed, with a higher number of particles per unit area compared to the state before oxidation. This fact was a consequence of Cr diffusion to the steel surface through the subsurface zone.

Micro-structural evolution of oxide scales formed on a Nb-Stabilizing heat-resistant steel at the initial stage in high-temperature water vapor

Steam Oxidation of Austenitic Heat-Resistant Steels TP347H and TP347HFG at 650–800 °C

Studies on the Oxidation Behavior and Microstructural Evolution of Two Nb-Modified HR3C Austenitic Steels under Pure Water Vapor at 650 °C

Microstructure understanding of high Cr-Ni austenitic steel corrosion in high-temperature steam

Investigation of Oxide Layer Development of X6CrNiNb18-10 Stainless Steel Exposed to High-Temperature Water

Effect of Nb Addition on Oxidation Mechanisms of High Cr Ferritic Steel in Ar–H2–H2O

Abnormal Growth Transport in Oxide Scales on Fe-16Cr Steels in Water Vapor

A Study of the Mechanism of Formation of Composite Oxide Scale on Heat-Resistant Steel 25Cr18Ni9Si2

Microstructural evolution of early-stage oxide film on 15–15Ti austenitic stainless steel under 500 °C steam

Experimental Study of the Evolution of Creep-Resistant Steel’s High-Temperature Oxidation Behavior

High-temperature oxidation behaviour of nanostructure surface layered austenitic stainless steel

Effect of Chromium and Water Vapor of Low Carbon Steel on Oxidation Behavior at 1050 °C

Microstructure evolution and corrosion behavior of Nb-alloyed cast heat-resistant steel during different aging treatments

Morphology and Buckling of the Oxide Scale after Fe–9Cr Steel Oxidation in Water Vapor Environment

The Process of Steam Oxidation Degradation of High Cr Steel after 125 000 Hours at 568 °C under 16.5 MPa

Microstructural Characteristics of the Oxide Scale Formed on 304 Stainless Steel in Oxygenated High Temperature Water

Field Studies of Steam Oxidation Behavior of Austenitic Heat-Resistant Steel 10Cr18ni9cu3nbn

Corrosion Behavior of Alumina-Forming Austenitic Steel in Supercritical Carbon Dioxide Conditions: Effects of Nb Content and Temperature

Oxidation Behavior of Al-Si Coating Modified TP347H FG in Saturated Steam at 650 ℃

Effects of precipitation on the scale and grain growth in 9% Cr tempered martensite steel upon steam oxidation

Oxide-Scale Evolution on a New Ni–Fe-Based Superalloy at High Temperature