Microwave Absorption in 0.1–18 GHz, Magnetic and Structural Properties of SrFe12-Ru O19 and BaFe12-Ru O19

Yidi Chang,Yanan Zhang,Lu Li,Shunquan Liu,Zhi Liu,Hong Chang,Xin'an Wang

DOI: https://doi.org/10.1016/j.jallcom.2019.152930

IF: 6.2

2020-01-01

Journal of Alloys and Compounds

Abstract:The hexagonal SrFe12O19 and BaFe12O19 ferrites have a high magnetocrystalline anisotropy due to the ions at the 2 b site. The axial component at the 2 b site is weakened by the Ru doping, as it is reflected in the xrd refinements and the FT-IR spectra. Accompanied with this, the coercivity of SrFe12-xRuxO19 decreases from 4.38 kOe in x = 0 to 0.68 kOe in x = 0.5 and 0.42 kOe in x = 1.5. That of BaFe12-xRuxO19 decreases from 2.47 kOe in x = 0 to 1.10 kOe in x = 1.0. With high magnetocrystalline anisotropies, the ferromagnetic resonance (FMR), above 40 GHz, of both BaFe12O19 and SrFe12O19 falls out of 0.1-18 GHz. In BaFe12-xRuxO19 with x >= 0.3, FMR is observed at 14.5 GHz in 0.1-18 GHz, but the reflection loss (RL) is very low with RL >=-10 dB. In SrFe12-xRuxO19, strong microwave absorptions with RL <=-10 dB in 0.1-18 GHz range are observed with 0.5 < x < 1.5. The optimum RL is -32 dB observed in x = 1.0 and 1.3, and the widest bandwidth is 6.55 GHz in x = 1.0 with the thickness as 2.3 mm. In x = 0.5, RL <=-10 dB occurs in 14.2-18 GHz. As the Ru content varies, the microwave absorption of SrFe12-xRuxO19 fully covers a large frequency range of 4.0-18 GHz. The Ru doping drives SrFe12-xRuxO19 (0.5 <= x <= 1.5) become good microwave absorbing materials in 0.1-18 GHz. (C) 2019 Elsevier B.V. All rights reserved.