Cations’ Ordering, Magnetic Properties and Strongly Enhanced Microwave Absorption Properties of La2NiMn1-Ru O6

Lan Zhang,Chao Gao,Chao Meng,Yuqi Zhang,Yue Hao,Lei Chen,Shunquan Liu,Hong Chang

DOI: https://doi.org/10.1016/j.ceramint.2020.02.185

IF: 5.532

2020-01-01

Ceramics International

Abstract:The properties of the A(2)BB'O-6 perovskites strongly depend on the cations' orderings at the B site. The cations' orderings of La2NiMn1-xRuxO6 are improved with the Ru doping especially in x = 0.5, as illustrated in the XRD patterns. It is also supported by the FT-IR spectra. The magnetic properties show that the x >= 1.0 sample is antiferromagnetic with the Neel temperature at 23 K. The antiferromagnetic transition is also observed in the other samples with the transition temperature slightly varying from 23 K to 38 K. In x = 0.1, one ferromagnetic transition is observed at 242 K, and it linearly decreases to 38 K in x = 0.8. The magnetic moments are calculated based on the superexchange model. From the comparison of the calculated and the measured one, it suggests that both ordered and disordered patches coexist in x = 0.1 and 0.3, while in x >= 0.5 the cations are fully ordered. The Ru doping increases the dielectric permittivity due to the enhanced dipolar polarization. The dielectric loss tangents are higher in x >= 0.5 than those in x = 0.1 and 0.3. In x = 0.8, the effective absorption with RL < -10 dB is able to cover the full frequency range of 2.2 GHz-18 GHz. In x = 1.0, the thickness with RL < -10 dB is as thin as 1.9 mm. Triple sets of microwave absorption peaks are observed. The quarterwavelength criteria explains the relationship between the optimum thickness and the frequency.