Effect of Thermal Annealing on a Cuboid DKDP Crystal

Duanyang Chen,Bin Wang,Hu Wang,Shenghao Wang,Kaizao Ni,Lili Zheng,Hui Zhang,Hongji Qi,Jianda Shao

DOI: https://doi.org/10.1016/j.jallcom.2019.152812

IF: 6.2

2020-01-01

Journal of Alloys and Compounds

Abstract:To further improve the quality of the cuboid DKDP crystal, the effect of thermal annealing at 160 degrees C were evaluated. After thermal annealing, the symmetry of the HRXRD of the X-cut sample is much better, indicating that the uniformity of the cuboid crystal is improved. The transmittance of annealed THGoriented sample is obviously higher than the as-grown THG-oriented sample from 400 to 300 nm. At 355 nm, the transmittance of the THG-oriented sample increases from 80.4% to 87.9% after thermal annealing. Besides, thermal annealing is also beneficial to the weak absorption properties at 355 nm of the X-cut cuboid DKDP crystal. The average weak absorption of the X-cut sample is decreased from 26.6 ppm to 12.3 ppm, and the standard deviation of the X-cut sample is decreased from 17.0 ppm to 4.8 ppm after thermal annealing. The LID performance of the THG-oriented sample is improved through thermal annealing, and the fluences corresponding to 50% probability of LID is increased from 13.4 to 14.8 J/cm(2)(@3ns, 355 nm). Also, the density of the defect with low LID threshold decreases by two-thirds. The above results indicate that thermal annealing is an effective means to further improve the quality of the cuboid DKDP crystal. (C) 2019 Elsevier B.V. All rights reserved.