Crystallization Kinetics Engineering toward High-Performance and Stable CsPbBr 3 -Based Perovskite Solar Cells
Chengben Liu,Teng Zhang,Zhi Li,Baohua Zhao,Xiaotong Ma,Yanli Chen,Zhaobin Liu,Haining Chen,Xiyou Li
DOI: https://doi.org/10.1021/acsaem.1c01593
IF: 6.4
2021-09-29
ACS Applied Energy Materials
Abstract:Due to their superior stability and high open-circuit voltage (Voc), all-inorganic cesium lead bromine (CsPbBr3) perovskite solar cells are attractive for tandem device applications. However, the current methanol fabrication process requires multistep (at least 5–6 times) spin coating, which is tedious and time-consuming. Here, we introduced a modified two-step spin-coating method to prepare the CsPbBr3 films. Water, instead of methanol, has been selected as the solvent for CsBr. Via precisely controlling the loading time (t) of CsBr aqueous solution on the PbBr2 film surface, the prepared films can be tuned from a CsPbBr3@CsPb2Br5 phase (t < 15 s) to a well-crystallized CsPbBr3 phase (t ∼ 15 s) and finally the CsPbBr3@Cs4PbBr6 phase (t > 15 s). With a loading time of 15 s, we yield a maximum power conversion efficiency (PCE) of 9.14%, which is comparable with the devices fabricated from the methanol process. In addition, a high fill factor (FF) of 0.84 with a PCE of 9.02% has been obtained, which is among the highest FF reported for CsPbBr3 devices. Moreover, the devices hold superior stability with their PCEs slightly dropped under humidity and high temperature during a 30 day aging test. Overall, this facile and simple fabrication method reported in this work shows great potential for practical applications in the future.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c01593.Experimental methods along with additional information, including preheating temperature dependent J–V curves; XRD patterns of the CsPbBr3 films from the methanol process; SEM–EDX data; EDX mapping spectrum; AFM images of the loading time-dependent CsPbBr3 films; spin coating speed and precursor concentration dependent J–V characterization; J–V curve with the highest FF; hysteresis feature; photovoltaic parameters; defect density; and TRPL time constant (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels