Abstract:Grain size engineering, particularly reducing grain size into the nanocrystalline regime, offers a promising pathway to further improve the strength-to-weight ratio of Al alloys. Unfortunately, the fabrication of nanocrystalline metals often requires non-equilibrium processing routes, which typically limit the specimen size and require large energy budgets. In this study, multiple dopant elements in ternary Al alloys are deliberately selected to enable segregation to the grain boundary region and promote the formation of amorphous complexions. Three different fully dense bulk nanocrystalline Al alloys (Al-Mg-Y, Al-Fe-Y, and Al-Ni-Y) with small grain sizes were successfully fabricated using a simple powder metallurgy approach, with full densification connected directly to the onset of amorphous complexion formation. All the compositions demonstrate densities above 99% with grain sizes <60 nm following consolidation via hot pressing at 585 °C. The very fine grain structure results in excellent mechanical properties, as evidenced by nanoindentation hardness values in the range of 2.2-2.8 GPa. Detailed microstructural characterization verifies the segregation of all dopant species to grain boundaries as well as the formation of amorphous complexions, which suggests their influential role in aiding effective consolidation and endowing thermal stability in the alloys. Moreover, nanorods with a core-shell structure are also observed at the grain boundaries, which likely contribute to the stabilization of the grain structure while also strengthening the materials. Finally, intermetallic particles with sizes of hundreds of nanometers form in all systems. As a whole, the results presented here demonstrate a general alloy design strategy of segregation and boundary evolution pathway that enables the fabrication of multiple nanocrystalline Al alloys with hierarchical microstructures and improved performance.

Formation of Refined Grains below 10 Nm in Size and Nanoscale Interlocking in the Particle-Particle Interfacial Regions of Cold Sprayed Pure Aluminum

Refining Micron-Sized Grains to Nanoscale in Ni-Co Based Superalloy by Quasistatical Compressive Deformation at High Temperature

Interfacial structure between particles in an aluminum deposit produced by cold spray

Grain Refinement of Pure Al Coating Via In-Situ Shot-Peening-Assisted Cold Spray

Nanocrystallization of interfacial microstructure of deformed particles in cold sprayed Ti6Al4V deposits

Bulk Nanostructure Formation Directly From The Multicomponent Alloy Melt

Structure and mechanical behavior of ultrafine-grained aluminum-iron alloy stabilized by nanoscaled intermetallic particles

Influence of Grain Size in the Near-Micrometre Regime on the Deformation Microstructure in Aluminium

Grain Refinement Mechanisms of TiC0.5N0.5 Nanoparticles in Aluminum

Bulk nanocrystalline Al alloys with hierarchical reinforcement structures via grain boundary segregation and complexion formation

Fabrication of Fine Grain Structures in Al Matrices at Elevated Temperature by the Stimulation of Dual-Size Particles

Influence of Friction Stir Spot Processing on Grain Structure Evolution and Nanomechanical Behavior of Cold-Sprayed Al Coating on Ti Substrate

Deformation induced grain boundary segregation in nanolaminated Al–Cu alloy

Formation of metastable phases in cold-sprayed soft metallic deposit

The Mechanisms of Enhancement of Inter-Particle Bonding in In-Situ Micro-Forging Assisted Cold Spray

Uncovering Microstructure Evolution and Dynamic Softening Mechanism of Spray-Deposited AlZnMgCu Alloy Under Thermal Deformation

Nanocrystalline Grain Structures Developed in Commercial Purity Cu by Low-Temperature Cold Rolling

Grain Size Dependent Plastic Behaviour in Bulk Nanocrystalline FeAl

Revealing the Mechanisms for the Nucleation and Formation of Equiaxed Grains in Commercial Purity Aluminum by Fluid-Solid Coupling Induced by a Pulsed Magnetic Field

Development of a material model for predicting extreme deformation and grain refinement during cold spraying

High-speed impact behavior of cold-sprayed Fe-based amorphous particle on Mg alloy substrate