Abstract:The calcite and vaterite type LuBO3:Eu3+ nano/microcrystals with various morphologies were synthesized by the hydrothermal (HT) approach through controlling the pH values of the precursor solutions. The calcite type LuBO3:Eu3+ shows the dominant magnetic dipole D-5(0)-F-7(1) emission due to S-6 inversion symmetry of Lu. It also shows a symmetrical O-Eu charge transfer (CT) excitation band, which, however, is asymmetrical and broad in the material prepared by the solid-state (SS) reaction method. The effect of the residual OH- groups introduced in HT synthesis is discussed on O-Lu exciton annihilation and local environment distortion. Two different Eu3+ centers, one of which is with inversion symmetry, are observed in vaterite type LuBO3:Eu3+ The HT sample with nanostructures, such as vaterite type flowerlike LuBO3:Eu3+, demonstrates a red shift of the CT band and appearance of a long excitation tail at the long wavelength side of the CT band. XRD, selective excitation and fluorescence decay measurements indicate that the red shift is induced by an increase of crystal lattice parameters, and the excitation tail is responsible to the Eu3+ ions located at lower symmetric sites. These sites are attributed to the positions at or close to the surface of the nanostructures in the sample. As the lower symmetric sites are selectively excited, the red emission of D-5(0)-F-7(2) of Eu3+ enhanced twice relatively to the orange emission of D-5(0)-F-7(1), exhibiting superior color chromaticity in red for display application. The luminescence properties of interior Eu3+ and outside Eu3+ are studied and discussed in detail.

Hydrothermal Epitaxy and Luminescent Properties of LaVO4:Cu,Eu Nanorod Array Films

Hydrothermal synthesis and photoluminescence of single-crystalline LaVO4:Eu3+ nanorods/nanosheaves

Monazite and Zircon Type LaVO4:Eu Nanocrystals - Synthesis, Luminescent Properties, and Spectroscopic Identification of the Eu3+ Sites

General synthesis and self-assembly of lanthanide orthovanadate nanorod arrays

Electrodeposition of high aspect ratio LaPO 4 and LaPO 4 :Ln 3+ (Ln 3 + =Ce 3+ , Tb 3+ ) nanostructures

Gastrointestinal complications after radiation therapy in patients with hepatocellular carcinoma.

Hydrothermal Synthesis and Luminescence Behavior of Rare-Earth-doped NaLa(WO4)2 Powders

Structural Transformation Induced Improved Luminescent Properties for LaVO4:Eu Nanocrystals

Luminescence Behavior of Eu3+ Doped LaF3 Nanoparticles.

Luminescent Properties in Relation to Controllable Phase and Morphology of Lubo3:Eu3+ Nano/Microcrystals Synthesized by Hydrothermal Approach

Synthesis process and the luminescence properties of rare earth doped NaLa(WO4)2 nanoparticles

Generalized Synthesis of NaLn(MoO4)2 Nano/microcrystals (ln = La–Lu and Y): the Effects of Lanthanide Contraction, Structure, and Down-/Up-conversion Luminescence

Facile surfactant- and template-free synthesis and luminescent properties of one-dimensional lu 2O 3:Eu 3+ phosphors

Electrophoretic Deposition and Photoluminescent Properties of Eu-doped BaTiO3thin Film from a Suspension of Monodispersed Nanocrystallites

Hydrothermal Synthesis and Photoluminescence Properties of La2−xEuxSn2O7 (x=0–2.0) Nanocrystals

Preparation and Luminescent Properties of 1d Lu2o2s:Eu3+ Nanorods

Facile Hydrothermal Synthesis and Luminescent Properties of Large-Scale GdVO<sub>4</sub>:Eu<sup>3+</sup>Nanowires

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Hydrothermal synthesis of hexagonal lanthanide-doped LaF3 nanoplates with bright upconversion luminescence

Controlled Synthesis and Luminescent Properties of Cubic Lu2O3:Eu3+ Nanocrystals

Controllable Synthesis and Luminescence Properties of One-Dimensional La2O3 and La2O3:Ln3+ (ln = Er, Eu, Tb) Nanorods with Different Aspect Ratios