Abstract:Ti2AlNb (Ti-22Al-25Nb at.%, nominal composition) intermetallic is essential to aerospace industry from a weight reduction perspective, and brings a possibility of replacing some Ni-based superalloys. Despite evaporation of element Al (from its original composition 22.8 at.% to 18.5 at.%), selective laser melting (SLM) technology offers distinct advantages in fabricating Ti2AlNb intermetallic with superior room-temperature properties. A full understanding of corresponding heat treatment mechanism is the key to utilize well the SLM-prepared Ti2AlNb at high temperatures. This study aims to clarify the relationship between the microstructure and mechanical propensities of SLM-prepared then heat-treated Ti2AlNb, to ultimately achieve promising mechanical performances at high temperatures. For this research purpose, a series of heat treatments were conducted, and the corresponding microstructures, mechanical properties were systematic studied by advanced characterization techniques. Results show that the mechanical properties at both room and high temperatures depend on heat treatment adopted. The samples solution-treated at 950 degrees C and then aged at 700 degrees C show promising room and high temperature strengths due to the formation of acicular O, alpha(2) and grain boundary alpha(2) phases. However, their ductility was poor. Aging at 830 degrees C reduces the strength, but significantly improves the ductility due to the appearance of rodlike O phase and the increase of B2/beta phase proportion. The alloy possesses promising strength and ductility (611 MPa, 10.0%) and high thermal stability at 650 degrees C. It is further demonstrated that the heat-treated Ti2AlNb possesses promising specific strength, even higher than that of as-cast Inconel 718 superalloy. The developed alloy, therefore, has a high potential for the industries requiring high-temperature performance and weight reduction.

Selective Laser Melting of Ti–22Al–25Nb Intermetallic: Significant Effects of Hatch Distance on Microstructural Features and Mechanical Properties

Selective Laser Melting Enabled Additive Manufacturing of Ti-22Al-25Nb Intermetallic: Excellent Combination of Strength and Ductility, and Unique Microstructural Features Associated

The effect of hatch distance on the microstructure and mechanical properties of Ti15Mo prepared by selective laser melting

Effect of Heat Treatments on the Microstructure and Mechanical Properties of Ti2AlNb Intermetallic Fabricated by Selective Laser Melting

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility

Selective laser melting of the hard-to-weld IN738LC superalloy: Efforts to mitigate defects and the resultant microstructural and mechanical properties

Effect of Scanning Strategies on the Microstructure and Mechanical Properties of Ti-22Al-25Nb Alloy Fabricated through Selective Laser Melting

Microstructure and Mechanical Property of Ti–5Al–5Mo–5V–3Cr–1Zr Alloy Fabricated by Selective Laser Melting with a Preheated Substrate

Role of processing parameters on relative density, microstructure and mechanical properties of selective laser melted titanium alloy

Selective laser melted near-beta titanium alloy Ti-5Al-5Mo-5V-1Cr-1Fe: Microstructure and mechanical properties

Effect of In-Situ TiB2 Particles on Microstructure and Mechanical Properties of Al–Fe–Ni Manufactured by Selective Laser Melting

Effect of Process Parameters on the Microstructure and Properties of Cu–Cr–Nb–Ti Alloy Manufactured by Selective Laser Melting

Hybrid Fabrication of Cold Metal Transfer Additive Manufacturing and Laser Metal Deposition for Ti6Al4V: The Microstructure and Dynamic/Static Mechanical Properties

Selective Laser Melting of High-Strength TiB2/AlMgScZr Composites: Microstructure, Tensile Deformation Behavior, and Mechanical Properties

Effects of Defects and Microstructures on Tensile Properties of Selective Laser Melted Ti6Al4V Alloys Fabricated in the Optimal Process Zone

The effect of process parameters on the physical and mechanical properties of Ti fabricated by selective laser melting using ball milled powders

Performance of Ti6Al4V fabricated by electron beam and laser hybrid preheating and selective melting strategy

Effect of Volume Energy Density on Selective Laser Melting Niti Shape Memory Alloys: Microstructural Evolution, Mechanical and Functional Properties

Process Optimization and Microstructure Characterization of Ti6Al4V Manufactured by Selective Laser Melting

Selective Laser Melting of Ti6Al4V: Effects of Heat Accumulation Phenomena due to Building Orientation