Bismuth-doped Germanate Glass Fiber Fabricated by the Rod-in-tube Technique
Ziyang Zhang,Jiangkun Cao,Jiayu Zheng,Mingying Peng,Shanhui Xu,Zhongmin Yang
DOI: https://doi.org/10.3788/col201715.121601
IF: 2.56
2017-01-01
Chinese Optics Letters
Abstract:Bismuth (Bi)-doped laser glasses and fiber devices have aroused wide attentions due to their unique potential to work in the new spectral range of 1 to 1.8 pm traditional laser ions, such as rare earth, cannot reach. Current Bi-doped silica glass fibers have to be made by modified chemical vapor deposition at a temperature higher than 2000 degrees C. This unavoidably leads to the tremendous loss of Bi by evaporation, since the temperature is several hundred degrees Celsius higher than the Bi boiling temperature, and, therefore, trace Bi (50 ppm) resides within the final product of silica fiber. So, the gain of such fiber is usually extremely low. One of the solutions is to make the fibers at a temperature much lower than the boiling temperature of Bi. The challenge for this is to find a lower melting point glass, which can stabilize Bi in the near infrared emission center and, meanwhile, does not lose glass transparency during fiber fabrication. None of previously reported Bi-doped multicomponent glasses can meet the prerequisite. Here, we, after hundreds of trials on optimization over glass components, activator content, melting temperature, etc., find a novel Bi-doped gallogermanate glass, which shows good tolerance to thermal impact and can accommodate a higher content of Bi. Consequently, we successfully manufacture the germanate fiber by a rod-in-tube technique at 850 degrees C. The fiber exhibits similar luminescence to the bulk glass, and it shows saturated absorption at 808 nm rather than 980 nm as the incident power becomes higher than 4 W. Amplified spontaneous emissions are observed upon the pumps of either 980 or 1064 nm from germanate fiber.