Abstract:Hafnium carbide (HfC) phase, with a high melting point, excellent strength, and high electrical conductivity, could be a suitable addition to enhance the microwave absorption properties of one-dimensional silicon carbide (SiC) nanomaterials without sacrificing its high-temperature thermal stability. In the present work, HfC/SiC hybrid nanofiber mats with different HfC loading contents are fabricated by electrospinning and high-temperature pyrolysis. HfC hybrids with sizes of 5-10 nm are embedded in the SiC nanofibers. As the HfC content increases from 0 to 6.3 wt %, the average diameter of the fibers drops from 2.62 μm to 260 nm. Meanwhile, the electrical conductivity rises from 7.9 × 10-8 to 4.2 × 10-5 S/cm. Moreover, the flexibility of the nanofiber mats is also greatly improved, according to a 200-times 180° bending test. Furthermore, compared with pure SiC fiber mats, the HfC/SiC nanofiber mats possess much larger dielectric loss because of higher electrical conductivity. At the optimal HfC content of 2.5 wt %, the HfC/SiC nanofibers/silicon resin composite (10 wt %) exhibits a minimal reflection loss (RL) of -33.9 dB at 12.8 GHz and a 3 mm thickness with a broad effective absorption bandwidth (RL < -10 dB) of 7.4 GHz. The above results prove that introducing HfC into SiC nanofiber mats is an effective way to enhance their flexibility, dielectric properties, and microwave absorption performance.

Effect of HfC Nanowires Grown on Carbon Fibers on the Microstructure and Thermophysical Properties of C/C Composites

Effects of HfC/PyC Core-Shell Structure Nanowires on the Microstructure and Mechanical Properties of Hf1-xZrxC Coating

Properties of Carbon Nano-Tubes–cf/sic Composite by Precursor Infiltration and Pyrolysis Process

Enhanced Interfacial Properties of High-Modulus Carbon Fiber Composites Via Molecular Assembly on Fiber Surface

The catalyst-free controllable growth behavior and mechanism of HfCnws on C/C composites

Ultra-high temperature resistance of one-dimensional hafnium carbide wrapped with pyrolytic carbon up to 2450 °C

Synthesis and Characterization of Single Crystalline Hafnium Carbide Nanowires

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

The effect of carbon nanotubes on the microstructure and morphology of pyrolytic carbon matrices of C–C composites obtained by CVI

3C-SiC Nanowires In-Situ Modified Carbon/Carbon Composites and Their Effect on Mechanical and Thermal Properties

Carbon Nanofiber Arrays Grown on Three-Dimensional Carbon Fiber Architecture Substrate and Enhanced Interface Performance of Carbon Fiber and Zirconium Carbide Coating.

Enhanced Flexibility and Microwave Absorption Properties of HfC/SiC Nanofiber Mats.

Synthesis and Characterization of Nano-Crystalized HfC Based on an Aqueous Solution-Derived Precursor.

Fabrication, Microstructural Evolution, and Mechanical Properties of SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C Nanocomposites

Effects of carbon nanotube length on interfacial properties of carbon fiber reinforced thermoplastic composites

Pyrolytic Synthesis of Conical Carbon Fibers with Carbon Nanotube Tips on Carbon Substrates

Characterization of Carbon Nanofiber Composites Synthesized by Shaping Process

Effect of Interfacial Structure on the Thermal Conductivity of Carbon Nanofibers Reinforced Aluminum Nitride Composites

Study on C/C composites modified by in-situ vapor-grown carbon nanofibers

Synthetic Hierarchical Nanostructures: Growth of Carbon Nanofibers on Microfibers by Chemical Vapor Deposition