Effect of forging speed on the formability, microstructure and mechanical properties of isothermal precision forged of Al–Zn–Mg–Cu alloy

Jiuhui Zhao,Yunlai Deng,Jin Zhang,Jianguo Tang

DOI: https://doi.org/10.1016/j.msea.2019.138366

2019-01-01

Abstract:An Al–Zn–Mg–Cu support bracket forging was isothermal precision forged at 400 °C with speeds of 0.1 mm/s, 0.01 mm/s and transient speed changing from 1 mm/s to 0.01 mm/s by finite element simulation and experiment. The stress concentration at high ribs of the simulated forging corresponded to the defects of under-filling and folding of the experimental forging at the speed of 0.1 mm/s while none defects appeared at the speeds of 0.01 mm/s and transient speed. Besides, not only less time was used to finish forging but also much more fine grains and sub-grains were formed in the forging that precision forged at the transient speed as compared with that at the speed of 0.01 mm/s, which leaded to the higher mechanical properties. Furthermore, the resistance to IGC was much better in the forging that precision forged at the transient speed for the particles η distributed along the grain boundaries was much wider.