Abstract:The 2195 Al-Cu-Li alloy is widely utilized in the aerospace industry due to its lightweight nature and high strength. Consequently, gaining a comprehensive understanding of techniques to enhance its microstructural and mechanical properties is crucial for the consistent production of reliable and high-strength aerospace components. In this investigation, a pristine 2195 industrial ingot was subject to three distinct forging pretreatments: PT1, which involved a direct three upsetting and three stretching (3U3S) process; PT2, which combined double stage homogenization (DH) with 3U3S; and PT3, which involved DH along with six upsetting and six stretching (6U6S). Subsequent warm deformation and T8 aging treatment were applied to the pretreated forgings. The microstructure evolution during the processes and the final mechanical properties in three orthogonal dimensions were examined. The findings revealed that the combination of DH and multi-dimensional forging (MDF) facilitated the dissolution of non-equilibrium phases to a greater extent. Consequently, the main strengthening phase transformed from the T 1 + δ` phase observed in PT1 to the denser T1 + little θ` phase observed in PT2 and PT3 after T8 aging treatment. Notably, the tensile strength and yield strength of PT2 and PT3 specimens increased by 20-30 MPa in all three directions. Moreover, the MDF process accelerated the recrystallization behavior from PT1 to PT3, resulting in a gradual reduction in the average grain size of the pretreated samples from 356 μm to 186 μm. Following warm forging and T8 aging, the grains exhibited a finer and equiaxed structure. Additionally, the coarse phase was identified as the primary source of transgranular cracking. The coarse phases within the matrix became more homogeneous and finer from PT1 to PT3, with a gradual decrease in their area fraction. On the fracture surfaces, the aggregation of coarse phases diminished. Consequently, the elongation in the z-direction improved, and the elongation anisotropy and standard deviation decreased in all three directions for PT3 specimens. The findings presented in this study provide valuable insights into the high-performance manufacturing of Al-Cu-Li alloys.

An innovative thermal simulation study of microstructure improvement by delay forging during solidification

Effect of Forging on Microstructure and Properties of Al-9Si-5Cu-0.2Zr-0.1Sr-0.16Ti-0.1Ce Cast Aluminum Alloy

Effect of Holding Time on Improving the Microstructure and Mechanical Properties of Die-Forged Az80-Ce Magnesium Alloys

Microstructure and mechanical properties of 6061 aluminum alloy prepared by casting-forging integrated technology

Influence of Forging Temperature on the Microstructures and Mechanical Properties of a Multi-Directionally Forged Al–Cu–Li Alloy

Numerical Simulation of Process and Grain Size for Large-Sized Aluminum Alloy 7050 Forging

Microstructural evolutions and mechanical properties of 6082 aluminum alloy part produced by a solution-forging integrated process

Effect of forging speed on the formability, microstructure and mechanical properties of isothermal precision forged of Al–Zn–Mg–Cu alloy

Numerical Simulation and Experimental Investigation on Multi-direction Forging Behaviors of High Purity Aluminum

Effect of forging pretreatment on the microstructures and mechanical properties of the Al-Cu-Li alloy

A new forging technology of 19 tons flat ingot with semi-solid liquid core

Investigation on Mechanism of Microstructure Evolution During Multi-Process Hot Forming of GH4169 Superalloy Forging

Numerical simulation of casting-forging integrated breakdown process

Increasing Strength and Ductility of a Mg–9Al Alloy by Dynamic Precipitation Assisted Grain Refinement During Multi-Directional Forging

Microstructure evolution and enhanced mechanical properties of additive manufacturing Al-Zn-Mg-Li alloy via forging and aging treatment

Effect of Temperature Filed on Microstructure of 7075 Aluminum Alloy in Multidirectional Forging Process

Optimization of multi-directional forging parameters of large-scale Mg-Gd-Y-Zn-Zr alloy forged part guided by finite element simulation

Optimization of Quasi-Β Forging Parameters to Control Trimodal Microstructure Parameters and Performance of TC21 Forgings

Phase Transformation and Dynamic Recrystallization Behavior of a Β-Solidifying Γ-Tial Alloy and Its Wrought Microstructure Control

Effects Of Forging Process Parameters On Microstructuire Evolution Of Alloy 7050

The Effect of the Forging Process on the Microstructure and Mechanical Properties of a New Low-Cost Ti-5Al-1.5Mo-1.8Fe Alloy