Abstract:Ethylene is one of the largest chemical products in the world, and its global demand increases significantly every year. At present, ethylene is mainly produced commercially through steam cracking of naphtha or alkane feedstocks. Catalytic dehydrogenation of ethane can effectively reduce energy loss of steam cracking. The transition metal Ni is a metal element with abundant reserves on the earth. It is widely used in the catalytic fields of hydrodesulphurization and reforming hydrogen production. However, there are few studies on Ni-based catalysts in alkanes dehydrogenation; therefore, three kinds of Ni-based supported catalysts, namely spinel decomposition-type, impregnation-type and perovskite precipitation-type, were prepared by different methods and explored for their performance in ethane dehydrogenation at 700 C in C2H6-N-2 atmosphere at 50 mL.min(-1). The results show that the spinel decomposition-type catalyst Ni1-xCuxCr2O4 prepared by glycine combustion method formed Ni-Cu alloy particles on the surface of Cr2O3 after reduction, which effectively passivated the C-C bond breaking activity of Ni and improved the selectivity of ethylene. The effect of Cu addition can be explained in geometric effect and electronic effect When the Ni content was too high, the Ni particles could not be effectively dispersed, forming large metal clusters and resulting in excessive cracking of ethane and low ethylene selectivity. The impregnation-type catalyst NixMy/Al2O3 (M=Cu or Ag) had a large specific surface area and dispersed surface active sites, but the active metal particles were weakly interacted with the support and unstable at high temperatures; Cu or Ag forming an alloy with Ni effectively unproved the selectivity of ethylene with Ag superior to Cu. The perovskite precipitation-type catalyst LaCr1-xNixO3 (LCNi-100x) precipitated unifonn and fine Ni particles in a reducing atmosphere, which were strongly bonded to the support and demonstrated high carbon deposition resistance and high stability; the reduced LCNi-15 (R-LCNi-15 containing 15% Ni) showed the best catalytic performance with the highest ethylene yield (24%), and high carbon deposition resistance and stability compared to commercial 13% CrOx/Al2O3. Moreover, carbon-deposited R-LCNi-15 can restore catalytic activity by oxidation regeneration.

Lanthanum Manganite-Based Perovskite As a Catalyst for Co-Production of Ethylene and Hydrogen by Ethane Dehydrogenation

LaMnO3-based Perovskite with In-Situ Exsolved Ni Nanoparticles: a Highly Active, Performance Stable and Coking Resistant Catalyst for CO2 Dry Reforming of CH4

High Performance Ni Exsolved and Cu Added La0.8Ce0.2Mn0.6Ni0.4O3-based Perovskites for Ethanol Steam Reforming

K/LaFeMnO3 Perovskite-Type Oxide Catalyst for the Production of C2–C4 Olefins via CO Hydrogenation

Efficient Hydrogen Production by Combined Reforming of Methane over Perovskite-Derived Promoted Ni Catalysts

The Ni Catalyst Supported on the FSP-made Transition Metal (Co, Mn, Cu or Zn) Doped La2O3 Material for the Dry Reforming of Methane

Performance and Improvement of Ni-based Catalysts for Ethane Dehydrogenation

Enhanced Thermochemical H2 Production on Ca-Doped Lanthanum Manganite Perovskites Through Optimizing the Dopant Level and Re-oxidation Temperature

Na2WO4/Mn/SiO2 Catalyst for Oxidative Dehydrogenation of Ethane Using CO2 As Oxidant

Alkali-metal enhanced LaMnO3 perovskite oxides for chemical looping oxidative dehydrogenation of ethane

Effect of Methane Co-Feeding on the Selectivity of Ethylene Produced from Oxidative Dehydrogenation of Ethane with Co2 over A Ni-La/Sio2 Catalyst

Surface in Situ Co-Mn Modification over LaMnO3 Perovskite with Enhanced Activity for Ethane Combustion

Lanthanum-mediated enhancement of nickel nanoparticles for efficient CO 2 methanation

Self-Assembly Dual Active Site Nanocomposite Anode Ce0.6Mn0.3Fe0.1O2−δ/NiFe/MnOx for Electrooxidative Dehydrogenation of Ethane to Ethylene

Lanthanum-Group Elements Promoted PtGa Catalysts for Propane Dehydrogenation: Exploring Key Performance Descriptors

Lanthanide Oxide Modified Nickel Supported on Mesoporous Silica Catalysts for Dry Reforming of Methane

Modification of Silica Supported Nickel Catalysts with Lanthanum for Stability Improvement in Methane Reforming with CO2

Partial Oxidation Of Methane To Carbon Monoxide And Hydrogen Over Nio/La2o3/Gamma-Al2o3 Catalyst

Oxidative Dehydrogenation of Ethane to Ethylene over Mesoporous Ni-Based Catalysts

La-promoted Na2WO4/Mn/SiO2 Catalysts for the Oxidative Conversion of Methane Simultaneously to Ethylene and Carbon Monoxide

Self-Assembly Dual Active Site Nanocomposite Anode Ce0.6Mn0.3Fe0.1O2-δ/NiFe/MnOx for Electrooxidative Dehydrogenation of Ethane to Ethylene.