Well‐defined synthesis of crystalline MnO, Mn2O3, and Mn3O4 phases by anodic electrodeposition and calcination
Roberto Cestaro,Bastian Rheingans,Peter Schweizer,Arnold Müller,Christof Vockenhuber,Claudia Cancellieri,Lars P. H. Jeurgens,Patrik Schmutz
DOI: https://doi.org/10.1111/jace.20081
IF: 4.186
2024-08-19
Journal of the American Ceramic Society
Abstract:The scalable synthesis of manganese oxide compounds with diverse physiochemical properties through anodic electrodeposition and calcination holds significant promise for applications ranging from photocatalysis to supercapacitors. Advanced characterization techniques unveiled crucial details about the compounds' morphology, crystal structure, porosity, and chemical state. A significant breakthrough was achieved by understanding the electrodeposition mechanism, resulting in a unique dual‐phase film of amorphous MnOOH and nanocrystalline α‐Mn3O4 under near‐neutral pH conditions. Moreover, this study deepens our understanding of phase transformation kinetics during calcination. Tailoring of the stoichiometry, crystallinity, and microstructure of manganese oxides (MnOx) is of utmost importance for technological applications in the field of catalysis, energy storage, and water splitting. In this work, α‐Mn2O3, α‐Mn3O4, and MnO thin films with defined stoichiometric compositions and crystal structures were prepared by calcination of an anodically electrodeposited Mn‐oxyhydroxide precursor film in different gas atmospheres (air, inert, or reducing gas). The crystal structure and composition of the precursor and product films were determined by combining X‐ray diffraction, transmission electron microscopy, Raman spectroscopy, Rutherford backscattering spectrometry, and elastic recoil detection analysis. The anodically electrodeposited precursor film consists of nanocrystals of α‐Mn3O4 dispersed in an amorphous MnOOH matrix phase, and can be fully transformed into either crystalline α‐Mn2O3, α‐Mn3O4, or MnO upon calcination in an oxidizing, inert or reducing atmosphere, respectively. In situ high‐temperature X‐ray diffraction was applied to derive the phase transformation kinetics, resulting in a corresponding activation energy which decreases in the order α‐Mn2O3 (268 kJ/mole) > MnO (102 kJ/mole) > α‐Mn3O4 (60 kJ/mole). The disclosed synthesis routes for the preparation of single‐phase MnOx films with a defined crystal structure and stoichiometry can be exploited for a wealth of applications.
materials science, ceramics