Improved lubrication and wear resistance of gallium-matrix liquid metal containing molybdenum diselenide nanoparticles under heavy load conditions
Shicheng Yan,Zhichao Xin,Yahong Xue,Haotian Zhang
DOI: https://doi.org/10.1016/j.wear.2023.204987
IF: 4.695
2023-05-25
Wear
Abstract:Owing to their advantages of high load-carrying performance, efficient heat conduction, and low friction coefficient, liquid metal-lubricated spiral groove bearings are critical mechanical components in high-speed mechanical support systems including computed tomography X-ray tubes, machine spindles of multi-axis numerical control machining center, etc. Therefore, it is imperative to understand the tribological mechanisms between liquid metal lubricants and tribo-pairs aiming to improve their functional properties and extend the service life of spiral groove bearings. In this study, molybdenum diselenide (MoSe 2 ) nanoparticles, a friction-reducing lubricant, were blended as an additive into the gallium-based liquid metal (LM, Ga 64 In 24 Sn 12 ) using mechanical grinding techniques. Following lubrication with MoSe 2 /Ga 64 In 24 Sn 12 LM lubricant, friction and wear characteristics of Si 3 N 4 ceramics ball/AISI 52100 steel disk friction pairs were evaluated by a high-frequency linear reciprocating oscillation friction test machine with ball-on-disc configuration under a normal load ranging from 50 N to 1500 N. Experimental results demonstrate that as the MoSe 2 dosage increases, the viscosity of MoSe 2 /Ga 64 In 24 Sn 12 LM lubricant gradually rises. Both normal load and MoSe 2 nanoparticles content have a notable influence on the lubrication properties of MoSe 2 /Ga 64 In 24 Sn 12 LM lubricant at a light (50 N) or a heavy load (1500 N). Of all these LM lubricants, the best lubrication performance and wear resistance ( f = 0.10, k = 1.93×10 −8 mm 3 /Nm) was achieved for 5.0 wt% MoSe 2 /Ga 64 In 24 Sn 12 . The improvement in the lubrication characteristics of MoSe 2 /Ga 64 In 24 Sn 12 LM lubricant under heavy load conditions originated from the generation of tribo-films from the Tribo-chemical reactions involving MoSe 2 nanoparticles. The thickness of Ga-based tribo-films is 1.50 ± 0.10 μm. This kind of tribo-films is rich in various nanocrystals consisting of orthorhombic α -Fe 2 O 3 , monoclinic β -Ga 2 O 3 , cubic In 2 O 3 , tetragonal rutile SnO 2 , orthorhombic α -MoO 3, and noncrystalline SiO 2 . Friction-induced lubricating films prevent adhesion wear of frictional pairs at heavy loads and consequently increase the load-bearing characteristics of LM lubricant, thereby improving the lubrication characteristics of LM.
engineering, mechanical,materials science, multidisciplinary