Abstract:Abstract To reduce the usage of classical lubricants in deep drawing, a new tribological system based on volatile lubricants was developed. Therefore, a volatile medium is injected under high pressure into the interstice between drawing tool and sheet metal. Depending on temperature and pressure, the temporary lubricant may exist in its gaseous or liquid phase. In this study, a novel high fluid pressure tribometer was designed to investigate the friction and wear of dry steel contacts under comparable conditions like in dry deep drawing. Therefore, a new ball-on-disc tribometer was designed and integrated into a high-pressure vessel. To specifically investigate the effects of different environments (technical air, liquid and gaseous carbon dioxide, nitrogen, argon) at atmospheric and high pressure (0.1 MPa, 6 MPa) on tribology, the specimens and all components were operating unlubricated. During the experiments, the friction was measured continuously. Results show that the highest friction occurs in air and the lowest in carbon dioxide environment. Subsequent to the experiments, the wear of the specimens was assessed along with changes in surface chemistry related to tribochemical reactions. Therefore, the tribology of the dry sliding contacts is correlated to changes of the surface chemistry. Also differences as well as similarities regarding the different fluid environments are shown. As the results show, the differences between the media used are most pronounced at elevated pressure. Concluding, this work gives clear indications on the suitability of volatile lubricants in dry friction or rather gas lubrication, especially for dry deep drawing.

What problem does this paper attempt to address?

The main aim of this paper is to study the effects of different environmental conditions (especially high-pressure gas environments) on the friction and wear characteristics of dry steel contact and to explore the potential application of volatile lubricants in the deep drawing process. To reduce the use of traditional lubricants, researchers have developed a new tribological system based on volatile lubricants. Specifically, the volatile medium is injected under high pressure into the gap between the drawing tool and the metal sheet. Depending on the temperature and pressure, this temporary lubricant may exist in a gaseous or liquid state. For this purpose, researchers designed a novel high-pressure fluid friction tester to simulate the friction and wear behavior of dry steel contact under conditions similar to dry deep drawing. The study experimentally investigated the effects of different environments (technical air, liquid and gaseous carbon dioxide, nitrogen, argon) on tribological characteristics under atmospheric and high-pressure conditions (0.1 MPa and 6 MPa). During the experiments, friction force was continuously measured, and post-experiment evaluations of wear and surface chemical changes of the samples were conducted. The results showed that the friction force was highest in the air environment and lowest in the carbon dioxide environment. Additionally, differences and similarities in friction and wear were observed between different fluid environments. These differences became more pronounced with increasing pressure. Overall, this work provides clear indications of the applicability of volatile lubricants in dry friction or gas lubrication, especially in the dry deep drawing process. In summary, the main objectives of the paper are: 1. To investigate the effects of different environments (especially high-pressure gas environments) on the friction and wear characteristics of dry steel contact. 2. To evaluate the ability of volatile lubricants to reduce friction and wear, particularly in the application of the dry deep drawing process.

Pressurized environments directly influence friction and wear of dry steel contacts—Investigations in a novel high fluid pressure tribometer

The Lubricity of Gases

Friction and Temperature Behavior of Lubricated Thermoplastic Polymer Contacts

Effect of Different Atmospheres on Dry Friction Behavior of Steel Sliding Against Brass at High Speed

Insights of the Ultralow Wear and Low Friction of Carbon Fiber Reinforced PTFE in Inert Trace Moisture Environment

Physicochemical Tribomechanics of Antifriction Materials Operating in Heavy-Loaded Friction Pairs in Active Lubricating Media

Grease-lubricated Tribological Behaviour of Nitrided Layer on 2cr13 Steel in Vacuum

A novel pressurised chamber to assess in-use durability performance of ceramic rolling contact elements using refrigerant lubrication

Analysis of the friction performance of deep-drawing steel sheets using network models

Experimental Study of Air Squeeze Effect on High-Frequency Friction Contact

Investigation of Graphene Platelet-Based Dry Lubricating Film Formation in Tribological Contacts

Tribological performance of lubricating oils with iron tribopairs under elevated temperature and pressure in carbon dioxide refrigerant

Understanding the Lubrication Regime Phenomenon and Its Influence on Tribological Characteristics of Additively Manufactured 316 Steel under Novel Lubrication Environment

Combined solid and liquid film lubrication for nanopositioning and nanomeasurement machines | Kombinierte fest- und flüssigschmierung für nanopositionier- und nanomessmaschinen

Environmental Atmosphere Effect on Lubrication Performance of Gallium-Based Liquid Metal

Humidity-dependent lubrication of highly loaded contacts by graphite and a structural transition to turbostratic carbon

Tribological studies of lubricated textured point contacts using MoS2 and PTFE nano oils under the reciprocating motion

Wear and Contact Temperature Evolution in Pin-on-Disc Tribotesting of Low-Metallic Friction Material Sliding Against Pearlitic Cast Iron

Experimental Investigation of Lubrication Properties at High Contact Pressure

Influence of microtextured parameters of dry gas sealing rings on tribological performance

Static friction measurement methodology for the assessment of performance of industrial valves at high temperatures: Case study for a nickel-based alloy coating