Hydration Characteristics and Microstructure of Magnesium Phosphate Cement in Presence of Cu2+

He Xin,Lai Zhenyu,Yan Tao,Wu Jie,Lu Zhongyuan,Lv Shuzhen,Li Feng,Fan Xiaoling
DOI: https://doi.org/10.1016/j.conbuildmat.2019.07.184
2019-01-01
Abstract:Heavy metal pollution is one of the severe problems facing the environment, and magnesium phosphate cement (MKPC) is increasingly used for the solidification/stabilization (S/S) treatment of heavy metals due to their excellent properties, the hydration characteristics and microstructure of MKPCs plays a key role in the S/S treatment of heavy metals, but this has not been sufficiently studied. In this study, the effects of Cu2+ on the hydration characteristics of MKPCs were analyzed using compressive strength, setting time, pH, heat of hydration, the phases and microstructure of samples were investigated by X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy measurements and Cu2+ leaching rate of samples were also measured. The results indicated that the addition of Cu2+ reduced the compressive strength of MKPCs and also delayed the setting time at high magnesia to potassium dihydrogen phosphate (M/P) ratios. When the addition of Cu2+ was 4%, the compressive strength of the sample cured 12 h decreased by 73% and the final setting time of the sample was prolonged by 94% with the M/P ratio of 4:1. Cu2+ did not affect the main hydration products of MKPCs, but lowered the change rate of the pH, got the smaller exothermic hydration peak, and reduced crystallinity of the main hydration product. Moreover, the leaching concentration (1.7 mg/L) of Cu2+ measured using the toxicity characteristics leaching procedure was lower than the TCLP (Toxicity Characteristic Leaching Procedure) requirement (15 mg/L). A lower M/P ratio is beneficial to improve the S/S performance of Cu-incorporated MPC. (C) 2019 Elsevier Ltd. All rights reserved.
What problem does this paper attempt to address?