Abstract:Two different morphologies of martensite in dual-phase (DP) steel were obtained through two processing routes. In the first method, the steel was water quenched from a fully austenitic state, followed by intercritical annealing (IA). In the second method, the steel was water quenched, cold rolled, and then subjected to intercritical annealing (C-IA). For IA and C-IA steels, the intercritical temperatures varied from 735 C-degrees to 765 C-degrees to obtain different fractions of ferrite. To understand the effect of ferrite content, morphology, and the orientation of ferrite/austenite on martensitic transformation, a combination of scanning electron microscopy, electron backscattered diffraction, and dilatometric tests were conducted. It was observed that layered martensite presented in IA samples, and blocky martensite appeared only at prior austenite boundaries at 765 C-degrees. In C-IA samples, equiaxed martensite grains were present, which become coarser by elevating the temperature to 765 C-degrees. In IA samples, martensitic transformation was much faster than in C-IA samples; the difference in martensitic transformation rate is particularly significant at lower annealing temperatures. Carbon enrichment of the partial austenite had a converse effect on the martensitic transformation at 745 C-degrees in both samples. The highest transformation rate was recorded in IA samples at 745 C-degrees among all IA and C-IA samples. The ferrite/martensite in IA samples maintained Kurdjumov-Sachs orientation relationship (K-S OR) with prior austenite and selected the same variant in the same block. Whereas, in polygonal samples, ferrite/martensite had an irrational OR with the prior austenite, no variant selection appeared in ferrite and martensite grains. Martensite nucleation accelerated on the ferrite surface when it had a K-S OR with the matrix grain, forming a low-energy interface with the ferrite. In contrast, ferrite surfaces irrationally oriented with the matrix grain did not promote martensite nucleation. This was likely due to the large misorientation and higher carbon build-up near the boundary during intercritical holding. The lower activation energy for martensitic nucleation in IA samples compared to C-IA samples resulted in an accelerated rate of martensite transformation in IA samples.

Revealing Orientation-Dependent Martensitic Transformation in a Medium Mn Steel by Micropillar Compression

Effect of Crystallographic Orientation on Quenching Stress During Martensitic Phase Transformation of Carbon Steel Plate

Experimental Investigation on a Novel Medium Mn Steel Combining Transformation-Induced Plasticity and Twinning-Induced Plasticity Effects

A Simple Variant Selection in Stress-Driven Martensitic Transformation

Orientation Dependence of Stress-Induced Martensitic Transformation in Quenched Ti-50.8at%Ni Single Crystals

Crystallography and Consequence of the Cubic-Tetragonal-orthorhombic Multi-Step Martensitic Transformations in MnNi Alloys

The Crystallographic Mechanism for Deformation Induced Martensitic Transformation Observed by High Resolution Transmission Electron Microscope

Martensitic Transformation in Submicron Cu-Al-Ni Pillar

On the mechanical heterogeneity in dual phase steel grades: Activation of slip systems and deformation of martensite in DP800

Deformation Behavior and the Mechanism of Micro-Scale Ti-10v-2fe-3al Pillars in Compression

Investigations on austenite stability and martensitic transformation kinetics of a medium Mn steel under different strain states

Achieving Ultrahigh Strength with Stable Plasticity by Stress-Induced Nanoscale Martensitic Transformation in Ti2448 Sub-Micron Pillars

Determination of the orientation relationship between austenite and incommensurate 7M modulated martensite in Ni–Mn–Ga alloys

Differences In Deformation Behaviors Caused By Microband-Induced Plasticity Of [001]- And [111]-Oriented Austenite Micro-Pillars

Deformation mechanism and microstructure evolution of medium-Mn AHSS under various loading conditions

In Situ Observation of Thermoelastic Martensitic Transformation of Cu-Al-Mn Cryogenic Shape Memory Alloy with Compressive Stress

Differences in Deformation Behaviors Caused by Microband-Induced Plasticity of [0 0 1]- and [1 1 1]-Oriented Austenite Micro-Pillars

Unconventional twin deformation of Ni-Mn-Ga 7M martensite under tension mediated by the collective lattice reorientation from a-c twin to b-c twin

Atomic-scale Understanding of Twin Intersection Rotation and Ε-Martensite Transformation in a High Mn Twinning-Induced Plasticity Steel

The Influence of Intercritical Temperature, Ferrite-Austenite Morphology, and Orientation Relationship on Martensitic Transformation in Dual Phase Steels

Early Martensitic Transformation in a 0.74C–1.15Mn–1.08Cr High Carbon Steel