Abstract:{1011}-{1012} double twin is the most common twin type being observed in the rolled AZ31 magnesium alloy, especially at low or moderate rolling temperature. Four types of rolled AZ31 magnesium alloy sheets were produced by rolling strong basal textured AZ31 plates at 150°C and 300°C respectively through different rolling paths by two passes till total reduction 17%. The rolling paths are normal and cross rolling respectively: the rolling directions of the two passes for normal rolling are mentally paralleled while perpendicular to each other for the cross rolling. Sheets are characterized in terms of microstructure and texture using optical microscope and scanning-electron microscope equipped with EBSD detector, and their mechanical performances are measured by uniaxial tensile tests at room temperature and a strain rate of 0.001 s -1. Tensile samples are cut parallel or perpendicular to the final rolling direction to obtain the mechanical anisotropies. The effects of the {1011}-{1012} double twins occurred during rolling on the microstructure, texture and mechanical properties of the rolled sheets are discussed and related to each other. The results show that the fraction of {1011}-{1012} double twins varies widely in different rolled sheets, which are determined by the rolling temperature. The twins in different rolled sheets are arranged in different ways. In the normal rolled sheets, the traces of twins are approximately perpendicular to the final rolling direction, while in the cross rolled sheets there are both traces of twins parallel and to the final directions. This phenomenon is related to the variant selection of twinning during rolling deformation. And the variant selection law is related to the rolling direction. For the same reason, the textures of twins in the rolled sheets produced through different paths are different. The textures of twins will add onto the bulks, and increases the textural difference between the bulks. The differences between mechanical properties of the rolled sheets are also related to the different textures and microstructures of the sheets caused by twins. © Right.

'',6,1 > Influence of Pre-Rolling on Microstructural Evolution of Non-Basal Textured Magnesium Alloy

The effect of grain size on texture evolution and mechanical properties of an AZ31 magnesium alloy during cold-rolling process

Insights into the evolution of texture and mechanical properties during warm rolling and annealing of Mg–2Zn-0.5Ca alloy

Microstructure and Texture Evolution of Mg-3Zn-1Al Magnesium Alloy During Large-Strain Electroplastic Rolling

Effect of texture types on microstructure evolution and mechanical properties of AZ31 magnesium alloy undergoing uniaxial tension deformation at room temperature

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Twinning Behavior of a Strongly Basal Textured AZ31 Mg Alloy During Warm Rolling

Effect of Al addition and rolling reduction on microstructure and texture evolution of Mg–3Sn alloy during high-speed rolling

Reduction per pass effect on texture traits and mechanical anisotropy of Mg–Al–Zn–Mn–Ca alloy subjected to unidirectional and cross rolling

Microstructure evolution and mechanical property of Mg-3Al alloys with addition of Ca and Gd during rolling and annealing process

The effect of {1011}-{1012} double twinning on the microstructure, texture and mechanical properties of AZ31 magnesium alloy sheet during rolling deformation

Microstructure, texture evolution and mechanical anisotropy of Mg-Gd-Y-Zn-Zr alloy sheets produced by unidirectional and cross rolling

The effect of {10¯11}–{10¯12} double twinning on the microstructure, texture and mechanical properties of az31 magnesium alloy sheet during rolling deformation

The improvement on mechanical anisotropy of AZ31 magnesium alloy sheets by multi cross-rolling process

Enhanced mechanical properties of AZ91 magnesium alloy by asynchronously large-strain high-efficiency rolling with bimodal grain structure

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Microstructure, Mechanical Properties and Texture Evolution of Mg–Al–Zn–La–Gd–Y Magnesium Alloy by Hot Extrusion and Multi-Pass Rolling

Effect of Warm Rolling on the Microstructure, Texture and Mechanical Properties of Extruded Mg–Zn–Ca–Ce/La Alloy

Obtaining Heterogeneous Microstructure and Enhanced Mechanical Properties in ECAP-Processed AZ61 Alloys via Single-Pass Rolling with Increased Rolling Reduction

Non-Basal Slip Induced Rare Earth Texture Evolution in Mg-14Gd-0.5Zr (wt.%) Alloy During the Traditional Hot Rolling