Abstract:Carbon coated LiFePO4 (LiFePO4/C) with different contents of high electron conductive iron phosphide phase was synthesized by an aqueous sol–gel method in a reductive sintering atmosphere. Different synthesis parameters were used for adjusting the microstructure and phase compositions of the products. The effects of the carbon coating and iron phosphides on the electrochemical properties of the LiFePO4/C electrodes were studied by means of testing the discharge capacities at rates of 0.1–5C (1C=170mAhg−1) and analyzing the CV curves. The results show that carbon coating in a content of 1.5wt.% derived from the carbon source of ethylene glycol greatly decreases the particle size of LiFePO4 in one order in the specific surface area, and significantly improves the rate capability of LiFePO4. The effect of the content of FeP on the capacity of the carbon coated LiFePO4 was different at different discharge rates. Increasing the content of FeP from 1.2 to 3.7wt.% slightly decreases the capacity of LiFePO4/C at low discharge rate (0.1C and 1C), but obviously increases the capacity of LiFePO4/C when the discharge rate is increased to 5C. For the carbon free sample, even it also has 1.8wt.% FeP, it still possesses poor capacity due to the large particle size of LiFePO4 and the lack of conductivity. And too much iron phosphides lowers the discharge capacity of the electrode since they are inert for the deinsertion/insertion of lithium ion.

Effect of Synthesis Temperature on the Structure and Electrochemical Performances of LiFePO4/C

Effect of Synthesis Temperature on Electrochemical Performances of LiFePO4/C Composites

Effect of calcination temperature on electrochemical performances of LiFePO4/C cathode material

Synergetic Effect of the Crystallinity, Particle Size of LiFePO4 and the In-Situ Introduced Fe2P on Its High-Rate Capability

Effects of carbon coating and iron phosphides on the electrochemical properties of LiFePO4/C

Synthesis of LiFePO4/C Composite Cathode Materials by Solid State Method Using Mixed Iron Sources

Preparation and Electrochemical Performance of LiFePO_4/C Using Fe_2O_3 As Raw Material

Effect of particle size on electrochemical performance of lithium iron phosphate materials

Effect of sintering time on the physical and electrochemical properties of LiFePO4/C composite cathodes

Synthesis of LiFePO 4 /C Composite Electrode with Enhanced Electrochemical Performance

Structure Optimization and the Structural Factors for the Discharge Rate Performance of LiFePO4/C Cathode Materials

Influence of sintering atmosphere on the physical and electrochemical of LiFePO4/C

Synthesis and Characterization of Lifepo4/C Prepared Via A Sol-Gel Method

Effect of Sintering-method on Electrochemical Performance of LiFePO_4/C Cathode Material

Synthesis and effect of forming Fe2P phase on the physics and electrochemical properties of LiFePO4/C materials

Effect of Morphology of Iron Phosphate Precursors on the Electrochemical Performance of Lithium Iron Phosphate

Optimization of Carbon Coatings on LiFePO4: Carbonization Temperature and Carbon Content

Effects of heating rate on morphology and performance of lithium iron phosphate synthesized by hydrothermal route in organic-free solution

SYNTHESIS AND CHARACTERIZATION OF <font>LiFePO</font><sub>4</sub>/<font>C</font> PREPARED VIA A SOL–GEL METHOD

Synthesis of LiFePO4/C composite electrode with enhanced electrochemical performance

Effects of Iron Sources on Structure and Electrochemical Properties of LiFePO4/C Prepared by Sol-Gel Method