Abstract:Capping layers (CPLs) are commonly employed in top-emitting organic light-emitting diodes (TEOLEDs) due to their ability to optimize color purity, enhance external light out-coupling efficiency, and improve device stability. However, the mismatch in refractive index between CPLs and thin film encapsulation (TFE) often induces light trapping. This study introduces a novel approach by combining a low refractive index material, lithium fluoride (LiF), with the traditional TFE material, silicon nitride (SiNx), to form a combined CPL (LiF/SiNx), resulting in improved light outcoupling and light reflection properties. The significant refractive index contrast between LiF and SiNx can facilitate enhanced light extraction by redirecting internally reflected light through evanescent waves. Moreover, the LiF/SiNx CPLs function as a secondary resonant cavity, leading to reduced emission spectral bandwidth and enhanced light extraction compared to the control TEOLEDs that only incorporate the primary cavity of organic active layers. As a result, incorporating the LiF/SiNx CPLs significantly increases current efficiency from 125.0 cd/A to 163.6 cd/A for green devices, from 71.2 cd/A to 110.1 cd/A for red devices, and from 43.1 cd/A to 53.1 cd/A for blue devices, with the corresponding full width at half maximum decreased from 20 nm to 10 nm, 26 nm to 14 nm, and 21 nm to 12 nm, respectively, demonstrating the compatibility of the CPLs to different color devices. Notably, an LT95 lifetime of 51,300 hours for green devices was achieved when tested at 1000 cd/m2. Utilizing narrow-band light emission without spectral overlap of each color enables the generation of purer and more vivid colors for display.

Highly Efficiency Top-Emitting Organic Light-Emitting Diode with Double Capping Layers

Highly Efficient Dual-Dopant Enhanced Emission OLEDs

Highly Efficient Nondoped Green Organic Light-Emitting Diodes with Combination of High Photoluminescence and High Exciton Utilization

Highly Efficient Top Emitting Organic Light-Emitting Diodes With Organic Outcoupling Enhancement Layers

Double-layer Printed White Organic Light-Emitting Diodes Based on Multicomponent High-Performance Illuminants

High Efficiency and Low Voltage P-I-n Top Emitting Organic Light-Emitting Devices

Improving the Performance of Red Organic Light-Emitting Transistors by Utilizing a High-k Organic/Inorganic Bilayer Dielectric.

Highly efficient OLED device based on the double emissive layer with an EQE about 39%

Highly Efficient Solution-Processed Blue-Green to Red and White Light-Emitting Diodes Using Cationic Iridium Complexes As Dopants

Significant Light Extraction and Power Efficiency Enhancement of Organic Light Emitting Diodes by Subwavelength Dielectric-Nanomesh Using Large-area Nanoimprint

Highly Efficient Blue Fluorescent OLEDs with Doped Double Emitting Layers Based on P-N Heterojunctions

Enhancement of Light Extraction of Green Top-Emitting Organic Light-Emitting Diodes with Refractive Index Gradually Changed Coupling Layers

High-efficiency organic light emitting diodes using high-index transparent electrode

Increasing the Efficiency of the Blue OLED Device with a Double-Emitting Layer Structure

High-efficiency and Low-Voltage P-I-n Electrophosphorescent OLEDs with Double-Doping Emission Layers

High Efficiency Red and White Organic Light Emitting Diodes based on Exciplex Host

A Green Top-Emitting Organic Light-Emitting Device with Single-Mode Resonance and Improved Performance by Using WO 3 Capping Layer

Extremely Low Roll-Off and High Efficiency Achieved by Strategic Exciton Management in Organic Light-Emitting Diodes with Simple Ultrathin Emitting Layer Structure

Correlation between optimized thicknesses of capping layer and thin metal electrode for efficient top‐emitting blue organic light‐emitting diodes

Improved color purity and efficiency by a coguest emitter system in doped red light-emitting devices

Narrowband Emission and Enhanced Stability in Top-Emitting OLEDs with Dual Resonant Cavities