Abstract:Via a traditional sintering process, (1-x) [0.85BaTiO(3)-0.15Bi(Mg2/3Nb1/3)O-3] - x Na0.5Bi0.5TiO3 (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1) (BT-BMN-NBT) ceramics were synthesized. The sintering temperature and density of the BT-BMN-NBT ceramics decreased with the increasing NBT content. All samples exhibited a pseudocubic phase and formed stable solid solutions with dense microstructures. The crystal structure of the BT-BMN-NBT ceramics gradually transformed from BT to NBT with increasing NBT content. The introduction of NBT with a high maximum polarization (P-max) could not only enhance the relaxor ferroelectric (RFE) characteristics of the BT-based RFE, but also compensate for the reduction in P-max of BT-based RFE that is due to the enhanced RFE characteristics. The temperature that corresponds to the maximum dielectric constant increases monotonously with the NBT content. P-max of the BT-BMN-NBT ceramics increases significantly as the NBT content increases. The best energy storage (ES) performances (x = 0.3) of a releasable energy density (W-rec) of 2.91 J/cm(3) and 85.55% efficiency were realized at 200 kV/cm. Compared with the unmodified BT-BMN ceramics (1.67 J/cm(3)), W-rec was improved by 1.48 times, which originated from the NBT modification induced increase in P-max (39.5 mu C/cm(2)) to 2.34 times the nominal BT-BMN value (16.9 mu C/cm(2)). The results prove that the addition of NBT could improve the ES performances of BT-based relaxor ferroelectrics at low-field by increasing the polarization.

Bi-fluctuation in Na0.5Bi0.5TiO3 Ferroelectric Ceramics with Abnormal Relaxor Behaviour

Dynamic Behavior of Polar Nanoregions in Re-Entrant Relaxor 0.6Bi(mg1/2ti1/2)o3-0.4Pbtio3

Size determination and dynamic behavior of polar nanoregions in re-entrant relaxor 0.6Bi(Mg$_{1/2}$Ti$_{1/2}$)O$_3$-0.4PbTiO$_3$

Large electrostrain in Bi1/2Na1/2TiO3-based relaxor ferroelectrics: A case study of Bi1/2Na1/2TiO3-Bi1/2K1/2TiO3-Bi(Ni2/3Nb1/3)O3 ceramics

An Experimental and Theoretical Investigation on Relaxor Behavior and Local Correlations in Xbi(zn0.5ti0.5)o3-(1-x)batio3 Ceramics

Re-entrant relaxor ferroelectric behaviour in Nb-doped BiFeO 3 –BaTiO 3 ceramics

Investigation of Lattice Evolutions of Tetragonal (Na0.5bi0.5)tio3-Batio3 Single Crystal by Phonon Modes in Raman Scattering

Strain evolution from the ferroelectric to the relaxor state in (0.67 - x)BiFeO3-0.33BaTiO3- x Bi(Mg0.5Zr0.5)O3 lead-free ceramics

Enhanced Relaxor Behavior and Thermal- and Frequency-Insensitive Strain of (na0.5bi0.5)0.93ba0.07ti1 − X(mn1/3nb2/3)xo3 Ceramics

Ferroelectric-Ferroelastic Transitions in (Na0.5bi0.5)tio3-Batio3 Single Crystals.

Dielectric Relaxor Evolution and Frequency‐Insensitive Giant Strains in (bi0.5na0.5)tio3‐modified Bi(Mg0.5Ti0.5)O3–PbTiO3 Ferroelectric Ceramics

Ferroelectric-Relaxor Behavior of 0.8Batio3-0.2(Na1/4bi3/4)(mg1/4ti3/4)o3 Ceramic

Thermal And Compositional Driven Relaxor Ferroelectric Behaviours Of Lead-Free Bi0.5na0.5tio3-Srtio3 Ceramics

Relaxation Behavior and Electrical Inhomogeneity in 0.9Batio(3)-0.1Bi (Mg1/2ti1/2)o-3 Ceramic

A Coexistence of Multi-Relaxor States in 0.5Bifeo3–0.5batio3

Ferroelectric stability and fatigue mechanism of BNKT ceramics by Nb doping

NaNbO3 modulated phase transition behavior and antiferroelectric stability evolution in 0.88(Bi0.5Na0.5)TiO3-0.12BaTiO3 lead-free ceramics

Evolution of the structure, dielectric and ferroelectric properties of Na<sub>0.5</sub>Bi<sub>0.5</sub>TiO<sub>3</sub>-added BaTiO<sub>3</sub>-Bi(Mg<sub>2/3</sub>Nb<sub>1/3</sub>)O<sub>3</sub> ceramics

Relaxor-like behaviors in Na1/2Bi1/2Cu3Ti4O12 ceramics

Quenching-induced nonergodicity in ergodic Na1/2Bi1/2TiO3–BaTiO3–AgNbO3 ceramics

Enhanced Rhombohedral Domain Switching and Low Field Driven High Electromechanical Strain Response in Bifeo3-Based Relaxor Ferroelectric Ceramics