Abstract:Antimony sulfide (Sb2S3) is an Earth-abundant and nontoxic material that is under investigation for solar energy conversion applications. However, it still suffers from poor power conversion efficiency and a large open circuit voltage loss that have usually been attributed to point or interfacial defects. More recently, there has been some discussion in the literature about the role of carrier trapping in the optical properties of Sb2S3 , with some reporting self-trapped excitons as the microscopic origin for the performance loss, while others have found no evidence of carrier trapping with only large polarons existing in Sb2S3 . By using first-principles methods, we demonstrate that Sb2S3 exhibits strong electron-phonon coupling, a prerequisite for carrier self-trapping in semiconductors, which results in a large renormalization of 200meV of the absorption edge when temperature increases from 10 to 300K . When two electrons or holes are added to the system, corresponding to a carrier density of 1.6×1020cm−3 , we find wave function localization consistent with the presence of bipolarons accompanying a significant lattice distortion with the formation of Sb and S dimers. The formation energies of the electron and hole bipolarons are −330 and −280 meV per carrier, respectively. Our results reconcile some of the controversy in the literature regarding carrier trapping in Sb2S3 and demonstrate the existence of large electron-phonon coupling and carrier self-trapping that might place a fundamental limit on the open circuit voltage and, consequently, the maximum efficiency of the photovoltaic cells. https://doi.org/10.1103/PhysRevMaterials.7.085401 Published by the American Physical Society under the terms of the Creative Commons Attribution 4.0 International license. Further distribution of this work must maintain attribution to the author(s) and the published article's title, journal citation, and DOI. Published by the American Physical Society

Ultrafast Self-Trapping of Photoexcited Carriers Sets the Upper Limit on Antimony Trisulfide Photovoltaic Devices

Suppressing the Trapping Process by Interfacial Charge Extraction in Antimony Selenide Heterojunctions

Engineering the charge extraction and trap states of Sb 2 S 3 solar cells

Coupled Electronic and Anharmonic Structural Dynamics for Carrier Self‐Trapping in Photovoltaic Antimony Chalcogenides

Sulfur Vacancies Limit the Open-circuit Voltage of Sb2S3 Solar Cells

Strong electron-phonon coupling and carrier self-trapping in Sb$_2$S$_3$

Strong electron-phonon coupling and bipolarons in

Structure, Morphology, and Photoelectric Performances of Te-Sb 2 Se 3 Thin Film Prepared via Magnetron Sputtering.

Both Free and Trapped Carriers Contribute to Photocurrent of Sb 2 Se 3 Solar Cells.

Intrinsic Trapping and Recombination Dynamics in Low‐Dimensional Bismuth Sulfide Nanocrystals

Structure, Morphology, and Photoelectric Performances of Te-Sb<sub>2</sub>Se<sub>3</sub>Thin Film Prepared via Magnetron Sputtering

Origin of Broadband Emission and Large Stokes Shift in Antimony Trisulfide

Structure, Morphology, and Photoelectric Performances of Te-Sb<sub>2</sub>Se<sub>3</sub> Thin Film Prepared via Magnetron Sputtering

Suppressing Buried Interface Nonradiative Recombination Losses Toward High-Efficiency Antimony Triselenide Solar Cells

A bithiophene-cored interfacial passivating layer for Sb2S3 solar cells with 7.1% efficiency

Sputtered and Selenized Sb2Se3 Thin-Film Solar Cells with Open-Circuit Voltage Exceeding 500 Mv

Negative-pressure Sulfurization of Antimony Sulfide Thin Films for Generating a Record Open-Circuit Voltage of 805 Mv in Solar Cell Applications

High Open‐Circuit Voltage in Full‐Inorganic Sb2S3 Solar Cell Via Modified Zn‐Doped TiO2 Electron Transport Layer

Upper efficiency limit of Sb2Se3 solar cells

High-Efficiency Flexible Sb2Se3 Solar Cells by Back Interface and Absorber Bulk Deep-Level Trap Engineering

Experimental disclosing the composition- and structure-dependent deep-level defect in photovoltaic antimony trisulfide materials