Nanoplasmonically Enhanced High-Performance Metastable Phase Α-Ga2o3 Solar-Blind Photodetectors

Guang Qiao,Qing Cai,Tongchuan Ma,Jin Wang,Xuanhu Chen,Yang Xu,Zhenguang Shao,Jiandong Ye,Dunjun Chen

DOI: https://doi.org/10.1021/acsami.9b13863

IF: 9.5

2019-01-01

ACS Applied Materials & Interfaces

Abstract:In this work, nanoplasmonic enhanced α-Ga2O3 solar-blind photodetectors with interdigital structure were fabricated on sapphire. By introducing Al nanoparticles (NPs) onto the device surface, the photodetector obtained a significant increase in responsivity at solar-blind region, and the response peak located at 244 nm reached 3.36 A/W under applied voltage of 5 V. Compared with the responsivity at 320 nm, the response ratio exceeds 240, demonstrating a superior solar-blind cut-off edge. It also presents that the photocurrent was dramatically increased under the 254 nm ultraviolet irradiation for the enhanced device while the dark current remains below 1 pA at 20 V. To explicitly elucidate the enhancement effects by Al NPs under ultraviolet illumination, Kelvin probe force microscopy was employed and directly revealed the physical mechanism of surface plasmon oscillation which promoted the formation of localized electric fields on α-Ga2O3. In addition, we illustrated the effects of interdigital spacing on device performances through experimental measurements and theoretical calculations. These results not only provide direct evidences for Al nanoplasmonic enhancement on α-Ga2O3 device, but also facilitate design and fabrication of solar-blind photodetectors.