Abstract:Recently, the manufacturing of porous polydimethylsiloxane (PDMS) with engineered porosity has gained considerable interest due to its tunable material properties and diverse applications. An innovative approach to control the porosity of PDMS is to use transient liquid phase water to improve its mechanical properties, which has been explored in this work. Adjusting the ratios of deionized water to the PDMS precursor during blending and subsequent curing processes allows for controlled porosity, yielding water emulsion foam with tailored properties. The PDMS-to-water weight ratios were engineered ranging from 100:0 to 10:90, with the 65:35 specimen exhibiting the best mechanical properties with a Young's Modulus of 1.17 MPa, energy absorption of 0.33 MPa, and compressive strength of 3.50 MPa. This led to a porous sample exhibiting a 31.46% increase in the modulus of elasticity over a bulk PDMS sample. Dowsil SE 1700 was then added, improving the storage capabilities of the precursor. The optimal storage temperature was probed, with −60 °C resulting in great pore stability throughout a three-week duration. The possibility of using these water emulsion foams for paste extrusion additive manufacturing (AM) was also analyzed by implementing a rheological modifier, fumed silica. Fumed silica's impact on viscosity was examined, revealing that 9 wt% of silica demonstrates optimal rheological behaviors for AM, bearing a viscosity of 10,290 Pa·s while demonstrating shear-thinning and thixotropic behavior. This study suggests that water can be used as pore-formers for PDMS in conjunction with AM to produce engineered materials and structures for aerospace, medical, and defense industries as sensors, microfluidic devices, and lightweight structures.

Demulsification-induced Fast Solidification: a Novel Strategy for Preparation of Polymer Encapsulations

The Polymer-rich Phase Solidification Process of PVDF-PVP-DMAc-H2O Solution

Emulsion Lyophilization as a Facile Pathway to Fabricate Stretchable Polymer Foams Enabling Multi-shape Memory Effect and a Clip Application.

Encapsulation of Phase Change Materials Via Interfacial Miniemulsion Polymerization for High Thermal Energy Storage Density

Nanoencapsulation of A Hydrophobic Compound by A Miniemulsion Polymerization Process

Preparation of microcapsules containing ionic liquids with a new solvent extraction system

Encapsulation of hygroscopic liquids via polymer precipitation in non-aqueous emulsions

Preparation of uniform microcapsules with silicone oil as continuous phase in a micro-dispersion process.

A Coordination Strategy to Achieve Instant Dissolution of a Biomedical Polymer in Water Via Manual Shaking.

Emulsion-templated formation of poly(N-isopropylacrylamide):surfactant mixed shells by thermo-enhanced interfacial complexation

Fabrication Of Metal-Organic Framework/Polymer Composites Via A One-Pot Solvent Crystal Template Strategy

Optimization of Shear Thickening Fluid Encapsulation Technique and Dynamic Response of Encapsulated Capsules and Polymeric Composite

Polysaccharide Assisted Microencapsulation for Volatile Phase Change Materials with a Fluorescent Retention Indicator

Encapsulation of shear thickening fluid as an easy-to-apply impact-resistant material

Porous Polymer Structures with Tunable Mechanical Properties Using a Water Emulsion Ink

Direct microencapsulation of Ionic-Liquid-Based shear thickening fluid via rheological behavior transition for functional applications

A facile approach for phase change material encapsulation into polymeric flexible fibers using microfluidic principles

ARTERIO-VENOUS FISTULAE AND RETICULO-ENDOTHELIAL ACTIVITY.

Encapsulation of Liquids via Polymer Precipitation in Emulsions

Hollow permeable polysiloxane capsules: a novel approach for fabrication, guest encapsulation and morphology studies