Abstract:1. Excellent microwave dielectric properties with a low ԑr ∼6.52, a high Q × f ∼46 010 GHz and a TCF∼−14ppm∘C−1 were obtained in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic sintered at 1060°C. 2. The 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics have excellent temperature stability. 3. The 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramics doped with LiF and LBSCA glass are suitable for LTCC technology due to their low sintering temperatures (from 830°C to 890°C) and good chemical compatibility with silver. In this work, the 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics were synthesized using a standard solid‐phase reaction process, and the inherent relationship between crystal structure and microwave dielectric properties was thoroughly explored. The crystal structure of the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic was determined by X‐ray diffractometer, which confirmed the existence of two phases. Microstructure observation of the ceramics was obtained by scanning electron microscope (SEM). Excellent microwave dielectric properties with a low ԑr ∼6.52, a high Q × f ∼46 010 GHz, and the temperature coefficient of resonant frequency (TCF) ∼−14 ppm°C−1 were obtained in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic sintered at 1060°C. By adding sintering additives LiF and Li2O–B2O3–SiO2–CaO–Al2O3 (LBSCA) glass, the sintering temperature was decreased from 1060°C to 870°C. Good microwave dielectric properties with a ԑr ∼6.59, a Q × f ∼18 820 GHz, and TCF ∼−14 ppm°C−1 were achieved in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ‐2 wt.% LiF, 1 wt.% LBSCA (2F1LBSCA) ceramic sintered at 870°C. The low‐temperature firing ceramics could also be well co‐fired with Ag with good chemical compatibility. These results indicated that the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic with 2F1LBSCA additions can be utilized in low‐temperature co‐fired ceramics technology to produce high‐frequency communication components.

Low temperature fired CaF2-based microwave dielectric ceramics with enhanced microwave properties

Low temperature fired CaF<sub>2</sub>-based microwave dielectric ceramics with enhanced microwave properties

Low-temperature Co-Fired Ceramics with High Thermal Expansion and Reliability for Millimeter-Wave Antennas

Low-Temperature Firing And Microwave Dielectric Properties Of Ca[(Li0.33nb0.67)(0.9)Ti-0.1]O3-Delta Ceramics With Lif Addition

Low‐temperature sintering of microwave ceramics with high Qf values through LiF addition

Low-fired Fluoride Microwave Dielectric Ceramics with Low Dielectric Loss

Low-temperature sintering and microwave dielectric properties of CaF2-doped MgTiO3 ceramics

Low-temperature firing and microwave dielectric properties of Ca[(LiNb)Ti]O ceramics with LiF addition

Low-temperature sintering and microwave dielectric properties of LiF-doped CaMg1−Zn Si2O6 ceramics

Low-temperature sintering and microwave dielectric properties of LiF-doped CaMg1-xZnxSi2O6 ceramics

Enhancement of densification and microwave dielectric properties in LiF ceramics via a cold sintering and post-annealing process

Modification of Low Temperature Sintered CMS Microwave Dielectric Ceramics Doped with Nanopowder

Low-fired (PbCa) (FeNb) O3 ceramics for multilayer microwave filter applications

Low-firing of CaAl2B2O7 ceramics with Li2O–B2O3–SiO2 and LiF additions

Cold sintering assisted CaF 2 microwave dielectric ceramics for C-band antenna applications

Microwave Dielectric Properties of Low Temperature Sintering Ca 5 Mn 4 (VO 4 ) 6 Ceramics

The Influence of CaF2 Doping on the Sintering Behavior and Microwave Dielectric Properties of CaO-B2O3-SiO2 Glass-Ceramics for LTCC Applications

LiCa3ZnV3O12: A Novel Low-Firing, High Q Microwave Dielectric Ceramic

Effect of LiF and LBSCA glass on the microwave dielectric properties of 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics for LTCC applications

Microwave dielectric properties of CaF2-doped ZnNb2O6 ceramics

Low Temperature Sinter-Ability of Microwave Dielectric Ceramics 0.4(Ca<sub>0.61</sub>Nd<sub>0.26</sub>)TiO<sub>3</sub>-0.6(Li<sub>0.5</sub>Sm<sub>0.5</sub>)TiO<sub>3</sub>