Abstract:Dielectric ceramics with low permittivity (epsilon(r)), high quality factor (Qxf), and near-zero resonant frequency (tau(f)) in the microwave bands are key materials used in fifth/sixth-generation (5G/6G) telecommunication, while tau(f) of most low-epsilon(r) microwave dielectric ceramics is relatively negative. In this work, the first low-epsilon(r) Ga-based ceramic SrGa12O19 with an anomalous positive tau(f) was reported, and the causes of the positive tau(f), intrinsic polarization, and loss mechanism were systematically studied. X-ray diffraction (XRD) and transmission electron microscopy (TEM) revealed that the SrGa12O19 ceramic formed a pure hexagonal magnetoplumbite structure with spinel blocks and rock-salt blocks stacked along the crystallographic c-axis. When sintered at 1430 degrees C, it possessed the optimal microwave dielectric properties of a low epsilon(r) of 14.46, high Qxf of 64,705 GHz, and exceptional positive tau(f) of +55.7 ppm/degrees C, along with a low linear thermal expansion coefficient (alpha(L)) of 11.617 ppm/degrees C. The large positive deviation between epsilon(r) and epsilon(r(C-M)) of 45.31% resulted from the rattling effect of atoms in the rock-salt block. The unique positive tau(f) (+55.7 ppm/degrees C) was governed by the rattling effect, resulting in a positive tau(alpha m) (the temperature coefficient of ion polarizability) of 8.489 ppm/degrees C and a large negative temperature coefficient of permittivity (tau(epsilon)) of -132.864 ppm/degrees C. Phillips-Vechten-Levine (P-V-L) chemical bond theory revealed greater contributions of the spinel block to bond ionicity (f(i), 52.95%), permittivity (epsilon, 55.15%), bond energy (E, 56.87%), and lattice energy (U, 74.88%) than those of the rock-salt block. The intrinsic dielectric properties were analyzed using infrared (IR) reflectivity spectra. The favorable performance of the SrGa12O19 ceramic indicated that it is a novel tau(f) compensator. This selection of compounds with different structural layer combinations provides a new idea for exploring excellent microwave dielectric ceramics.

Phase Composition and Microwave Dielectric Properties of Low Permittivity AGeO3 (A = Mg, Zn) Ceramics

SrGa12O19: the First Low-Εr Ga-based Microwave Dielectric Ceramic with Anomalous Positive Τf

Phase evolution, far-infrared spectra, and ultralow loss microwave dielectric ceramic of Zn 2 Ge 1+ x O 4+2 x (− 0.1 ≤ x ≤ 0.2)

Two Low-Permittivity Melilite Ceramics in the SrO-MO-GeO2 (M = Mg, Zn) System and Their Temperature Stability Through Compositional Modifications

Crystal structure and phase formation of MgO–MoO3‐based ceramics with ultralow dielectric loss: A comprehensive study

Microwave dielectric properties and phase evolution of Zn-excess Mg0.95Zn0.05+xTiO3+x (x = 0–0.1) ceramics

Three‐phase borate solid solution with low sintering temperature, high‐quality factor, and low dielectric constant

Synthesis and characterization of phase pure and Mg-modified AgZnVO 4 microwave dielectrics for high-frequency ULTCC applications

Phase structural characteristics and microwave dielectric properties of Ge-doped cordierite-based ceramics

Structure and infrared reflectivity spectra of novel Mg3Ga2GeO8 microwave dielectric ceramic with high Q

Crystal structure, Raman spectra and microwave dielectric properties of novel low-temperature cofired ceramic Li4GeO4

A novel low loss rare-earth germanate La4GeO8 microwave dielectric ceramic with orthorhombic structure

High-Qf value and temperature stable Zn2+-Mn4+ cooperated modified cordierite-based microwave and millimeter-wave dielectric ceramics

Two low-εr phenakite-structure LiAGeO4 (A = Al, Ga) microwave dielectric ceramics with different structure ordering

Unleashing the Potential of Mg2SiO4-based Ceramics for Millimeter-Wave Applications: Achieving Ultra-Low Loss with Enhanced Temperature Stability Through Heterovalent Ion Substitution

Ultra-low temperature sintering and temperature stable microwave dielectrics of phase pure AgMgVO4 ceramics

Microwave dielectric properties and chemical compatibility with alumina electrode of two novel ultra-low temperature firing ATeMoO6 (A = Mg, Zn) ceramics

Structure characteristics and microwave/terahertz dielectric response of low-permittivity (La0.2Nd0.2Sm0.2Eu0.2Gd0.2)2Zr3(MoO4)9 high-entropy ceramics

Ge-doped Li3+xMg2Nb1-xGexO6 ceramics with enhanced low loss and high temperature stability properties

Low temperature sintered MgO–based microwave dielectric ceramics with ultra‐low loss and high thermal conductivity

Microstructural evolution, dielectric performance, and densification behavior of novel NaAGeO4 (A = Sm, Y) ceramics