Abstract:Despite the high theoretical specific capacity and ultralow reduction potential advantages of Li anodes, dendrite growth in Li metal batteries leads to many problems. Realizing uniform Li deposition is the key to solving these problems, but it is usually difficult for traditional Li metal electrodes. In this study, CuO nanofilm-covered Cu microcones (NFMCs) on a Cu foil are prepared as current collectors to suppress Li dendrite growth and improve the electrochemical performance of the batteries. Li2O is in situ formed during the course of Li deposition according to the conversion reaction between CuO and Li. The nucleation energy barrier of Li is decreased due to high affinity between Li2O and Li. In addition, we found that Li2O also decreases the elastic strain energy at the interface between the deposited Li and the Li2O film, leading to uniform coverage of Li metal on microcones. The Li2O/Cu NFMCs show a coral-like structure instead of the sharp cone structure in Cu microcones. Thus, they can effectively mitigate the tip-charge effect, which will cause the continuous reduction of the Li ion at the tip. As a result, uniform and stable Li deposition without observation of the Li dendrite up to 1000 cycles at a current density of 5 mA cm–2 is achieved using this Li2O/Cu NFMC substrate. A full cell upon pairing with LiFePO4 achieves a high Coulombic efficiency of 96.7% for over 100 cycles at 0.2 C with a capacity retention over 92.7%.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.2c00218.Simulation model of the (a) Cu cone and (b) Li2O/Cu NFMC (2D axisymmetric graph); SEM image of the CuO layer directly forming on the Cu foil; nucleation overpotential of Li deposited on the CuO foil; SEM images of the growth process of the 2O/Cu foil; voltage–time curves of 2O/Cu NFMCs in symmetric cells with an area capacity of 4.5 mA h cm–2 at 13 mA cm–2 (5 mA h cm–2 Li previously deposited at 2 mA cm–2); voltage–time curves of 2O/Cu NFMCs, cones, and the 2O/Cu foil in symmetric cells with an area capacity of 1 mA h cm–2 at 1, 2, and 5 mA cm–2; Coulombic efficiency of Li2O/Cu NFMC and Cu cone current collectors with an area capacity of 1 mA h cm–2 at 2 mA cm–2; Nyquist plots of the 2O/Cu foil after various cycles in a symmetric cell with an area capacity of 1 mA h cm–2 at 1 mA cm–2; cycling performance of the LFP| foil full cell at 0.2 C; XPS spectrum of 2O/Cu NFMCs after Li deposition; and TEM image of a copper cone and HRTEM image of the cone edge (PDF)This article has not yet been cited by other publications.

In-Plane Highly Dispersed Cu2O Nanoparticles for Seeded Lithium Deposition

In Situ Synthesis of a Lithiophilic Ag-Nanoparticles-Decorated 3D Porous Carbon Framework Toward Dendrite-Free Lithium Metal Anodes

Vertically Aligned Lithiophilic CuO Nanosheets on a Cu Collector to Stabilize Lithium Deposition for Lithium Metal Batteries

Flaky and Dense Lithium Deposition Enabled by a Nanoporous Copper Surface Layer on Lithium Metal Anode

Seeding Lithium Seeds Towards Uniform Lithium Deposition for Stable Lithium Metal Anodes

CuO Nanofilm-Covered Cu Microcone Coating for a Long Cycle Li Metal Anode by in Situ Formed Li2O

<i>In situ</i> coating of a lithiophilic interphase on a biporous Cu scaffold with vertical microchannels for dendrite-free Li metal batteries

CuO Nanofilm-Covered Cu Microcone Coating for a Long Cycle Li Metal Anode by In Situ Formed Li 2 O

Lithium Induced Nano‐Sized Copper with Exposed Lithiophilic Surfaces to Achieve Dense Lithium Deposition for Lithium Metal Anode

Suppressing Lithium Dendrite Growth with Nanoparticle-Dispersed Colloidal Electrolytes

Long‐Range Uniform Deposition of Ag Nanoseed on Cu Current Collector for High‐Performance Lithium Metal Batteries

Lithiophilic Ag Nanoparticle Layer on Cu Current Collector toward Stable Li Metal Anode

Metal Oxide Nanoparticles Induced Step-Edge Nucleation of Stable Li Metal Anode Working under an Ultrahigh Current Density of 15 Ma Cm−2

Highly-lithiophilic Ag@PDA-GO film to Suppress Dendrite Formation on Cu Substrate in Anode-free Lithium Metal Batteries

Constructing Sn-Cu2O Lithiophilicity Nanowires As Stable and High-Performance Lithium Metal Anodes

In Situ Growth of CuO Submicro-Sheets on Optimized Cu Foam to Induce Uniform Li Deposition and Stripping for Stable Li Metal Batteries

Growing Cuprite Nanoparticles on Copper Current Collector Toward Uniform Li Deposition for Anode-Free Lithium Batteries

Lithiophilic Hyperbranched Cu Nanostructure for Stable Li Metal Anodes

Uniform Lithium Nucleation Guided by Atomically Dispersed Lithiophilic CoNx Sites for Safe Lithium Metal Batteries

Cu Nanoparticles Derived from CuO Electrodes in Lithium Cells

Regulating the Li Nucleation/Growth Behavior via Cu 2 O Nanowire Array and Artificial Solid Electrolyte Interphase toward Highly Stable Li Metal Anode