CuO Nanofilm-Covered Cu Microcone Coating for a Long Cycle Li Metal Anode by In Situ Formed Li 2 O
Wang Hu,Yiyuan Yao,Xiang Huang,Shenghong Ju,Zhuo Chen,Ming Li,Yunwen Wu
DOI: https://doi.org/10.1021/acsaem.2c00218
IF: 6.4
2022-03-15
ACS Applied Energy Materials
Abstract:Despite the high theoretical specific capacity and ultralow reduction potential advantages of Li anodes, dendrite growth in Li metal batteries leads to many problems. Realizing uniform Li deposition is the key to solving these problems, but it is usually difficult for traditional Li metal electrodes. In this study, CuO nanofilm-covered Cu microcones (NFMCs) on a Cu foil are prepared as current collectors to suppress Li dendrite growth and improve the electrochemical performance of the batteries. Li2O is in situ formed during the course of Li deposition according to the conversion reaction between CuO and Li. The nucleation energy barrier of Li is decreased due to high affinity between Li2O and Li. In addition, we found that Li2O also decreases the elastic strain energy at the interface between the deposited Li and the Li2O film, leading to uniform coverage of Li metal on microcones. The Li2O/Cu NFMCs show a coral-like structure instead of the sharp cone structure in Cu microcones. Thus, they can effectively mitigate the tip-charge effect, which will cause the continuous reduction of the Li ion at the tip. As a result, uniform and stable Li deposition without observation of the Li dendrite up to 1000 cycles at a current density of 5 mA cm–2 is achieved using this Li2O/Cu NFMC substrate. A full cell upon pairing with LiFePO4 achieves a high Coulombic efficiency of 96.7% for over 100 cycles at 0.2 C with a capacity retention over 92.7%.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.2c00218.Simulation model of the (a) Cu cone and (b) Li2O/Cu NFMC (2D axisymmetric graph); SEM image of the CuO layer directly forming on the Cu foil; nucleation overpotential of Li deposited on the CuO foil; SEM images of the growth process of the 2O/Cu foil; voltage–time curves of 2O/Cu NFMCs in symmetric cells with an area capacity of 4.5 mA h cm–2 at 13 mA cm–2 (5 mA h cm–2 Li previously deposited at 2 mA cm–2); voltage–time curves of 2O/Cu NFMCs, cones, and the 2O/Cu foil in symmetric cells with an area capacity of 1 mA h cm–2 at 1, 2, and 5 mA cm–2; Coulombic efficiency of Li2O/Cu NFMC and Cu cone current collectors with an area capacity of 1 mA h cm–2 at 2 mA cm–2; Nyquist plots of the 2O/Cu foil after various cycles in a symmetric cell with an area capacity of 1 mA h cm–2 at 1 mA cm–2; cycling performance of the LFP| foil full cell at 0.2 C; XPS spectrum of 2O/Cu NFMCs after Li deposition; and TEM image of a copper cone and HRTEM image of the cone edge (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels