Abstract:Introduction Shot peening (SP) is an important method to enhance metallic superficial properties [1-4]. After SP, the introduced compressive residual field (CRS) and change of microstructure could improve the surface properties significantly [5-7], such as surface microhardness, stress corrosion property, fatigue life, ect [8,9]. Stress peening is a special and important shot peening method. It is mainly used in stress peening forming to fabricate thin parts with complicated shapes, such as sheet with double curvatures, aerofoils. In the process of stress peening, specimens were elastically prebended in certain directions for peening forming. And a CRS field, a critical parameter for the component, were induced by high energy “shots”. After stress peening, the prestresses were released and the CRS field was changed by elastic recovery. This change could be considered as a superposition of two stress fields: one is a CRS field introduced by SP, another one is a stress field generated by release of the prestress. Specially, for different materials, the CRS field was different with same peening parameter and prestress [10-15]. Recently, the CNTs reinforced aluminium matrix composites have attracted wide and growing attentions to develop a new generation of high-stiffness metallic, high-strength, lightweight materials [16-22]. Due to it would be used for the fields of the electronic and military devices, high speed transportation. In these fields, the new material might be formed by stress peening to fabricate some complicated shapes. After stress peening, the CRS field induced by stress peening should be retained or released by annealing treatment due to specific requirements. In addition, few investigations have been made on thermal relaxation of an anisotropic CRS field.

Thermal Relaxation of Residual Stress in Shot-Peened CNT/Al–Mg–Si Alloy Composites

Thermal relaxation of residual stress in a carbon nanotube reinforced aluminium matrix composite

Surface Layer Characteristics of CNT/Al–Mg–Si Alloy Composites Treated by Stress Peening

Surface mechanical property and residual stress stability of nanostructured CNT/Al-Cu-Mg composites induced by shot peening

Residual stress and microstructure of the CNT/6061 composite after shot peening

Investigation for Different Peening Techniques on Residual Stress Field of SiCw/Al Composite

Thermal Relaxation of Residual Stresses in Shot Peened Surface Layer of SiCw/Al Composite

The residual stress varying of shot peened TC4-DT titanium alloy

Effect of Dual Shot Peening on Microstructure and Wear Performance of CNT/Al-Cu-Mg Composites

Residual Stress Field and Thermal Relaxation Behavior of Shot-Peened TC4-DT Titanium Alloy

Effect of Shot Peening on the Residual Stresses and Microstructure of Tungsten Cemented Carbide

Thermal Relaxation of Residual Stresses in Shot Peened Surface Layer on Tib2/Al Composite at Elevated Temperatures

Investigation on Microstructure and Properties of Al18B4O33 Whisker Reinforced AlMgSi Matrix Composite after Shot Peening

Effect of prestressed shot peening on residual stress and microhardness of C 63020 alloy

Surface shot peening of cast SiCw/Al composites

Effect of Stress Peening on Surface Layer Characteristics of (tib + TiC)/Ti–6Al–4V Composite

Influence of Isothermal Annealing on Stress Relaxation of Shot Peened SiCw/Al Composite

Surface Shot Peening of Cast SiC W /al Composites

Investigation on the Residual Stress and Microstructure of (tib+tic)/ti–6al–4v Composite after Shot Peening

Residual Stress Relaxation in Shot Peened Surface Layer on Tib2/Al Composite under Applied Loading

Effect of the Conventional Shot Peening and Multiple Shot Peening on Microstructure and Residual Stress of TC17 Titanium Alloy