Influences of La addition on the hydrogen storage performances of TiFe-base alloy
Tingting Zhai,Zhen Wei,Zeming Yuan,Zhonggang Han,Dianchen Feng,Haiyan Wang,Yanghuan Zhang
DOI: https://doi.org/10.1016/j.jpcs.2021.110176
IF: 4.383
2021-10-01
Journal of Physics and Chemistry of Solids
Abstract:<p>In this paper, La is partial substituted for Ti to improving the hydrogen storage performance of TiFe alloy. The Ti<sub>1-<em>x</em></sub>La<sub><em>x</em></sub>Fe<sub>0.8</sub>Mn<sub>0.2</sub> (<em>x</em> = 0, 0.01, 0.03, 0.06, 0.09) alloys were prepared by induction melting under vacuum. The influences of La on the microstructure, gaseous hydrogen absorption and thermodynamics were investigated. It was found from the X-ray diffraction results that all the alloys contained the single TiFe phase, the substitution of La does not change the phase composition of the alloys. The lattice parameters decreased with La substitution. And TiFeH and TiFeH<sub>2</sub> hydride were detected after hydrogenation process. The hydrogen absorption kinetic property of Ti<sub>1-<em>x</em></sub>La<sub><em>x</em></sub>Fe<sub>0.8</sub>Mn<sub>0.2</sub> (<em>x</em> = 0, 0.01, 0.03, 0.06, 0.09) alloys is improved by La substitution. The maximum hydrogen storage capacity of Ti<sub>1-<em>x</em></sub>La<sub><em>x</em></sub>Fe<sub>0.8</sub>Mn<sub>0.2</sub> (<em>x</em> = 0, 0.01, 0.03, 0.06, 0.09) alloys is 1.621, 1.633, 1.54, 1.532, 1.328 wt.%, respectively at 3 MPa 323K after activation. La substitution has significant effect on the P-C-T curves of the alloys, the plateaus pressure of TiFe to TiFeH heightened by La substitution increasing. Furthermore, the enthalpy and entropy changes of the hydrogenation/dehydrogenation at different temperatures were also calculated by Van't Hoff equation. The hydrogenation enthalpy Δ<em>H</em><sub>ab</sub> were -30.1, -31.7, -27.0, -27.7 and -27.4 kJ/mol H<sub>2</sub>, respectively.</p>
physics, condensed matter,chemistry, multidisciplinary