HRTEM and Nanoindentation Analysis of NiCoCrAlHfYSi and NiCoCrAlTaY Coatings Produced by AC-HVAF and APS

Yujun Han,Baosen Zhang,Xiaoyan Gu,Xinfa Qiang,Yajie Chu,Xiaoquan Li

DOI: https://doi.org/10.1016/j.surfcoat.2019.04.018

2019-01-01

Abstract:In this work, feedstock powders of NiCoCrAlHfYSi (Amdry386) and NiCoCrAlTaY (Amdry997) were deposited by atmospheric plasma spray (APS) and activated combustion high velocity air fuel (AC-HVAF), respectively. The research results show that the surface roughness of the HVAF386 and HVAF997 specimens increased considerably compared to the APS386 and APS997 specimens. The oxide contents decreased significantly in the two AC-HVAF specimens, and the pores and non-bonded interfaces are not easily observed. Additionally, the microstructures of the two feedstock powders were influenced significantly by the AC-HVAF and APS processes during coating deposition. Furthermore, the details of the microstructural characteristics of the four as-sprayed coatings were characterized by the HRTEM method, and various strengthening mechanisms of them were proposed. The strengthening of the APS386 specimen experienced sharp increase induced by the formation of twinning, whereas the strengthening mechanism of the APS997 specimen was likely due to presence of the superlattice second-phases distributed throughout the matrix gamma phase. Meanwhile, the elastic moduli and microhardness of the HVAF386 and HVAF997 specimens were enhanced significantly, suggesting the presence of stacking faults in the γ-matrix phase and the γ′-Ni3Al and β-(Ni,Co)Al precipitates at the boundaries of γ-(Ni,Co) grains, especially nano-precipitates in the HVAF386 specimen.