Influence of Cerium Content on the Corrosion Behavior of Al-Co-Ce Amorphous Alloys in 0.6 M NaCl Solution

L. M. Zhang,S. D. Zhang,A. L. Ma,A. J. Umoh,H. X. Hu,Y. G. Zheng,B. J. Yang,J. Q. Wang

DOI: https://doi.org/10.1016/j.jmst.2019.03.014

2019-01-01

Abstract:The effect of cerium content on the corrosion behavior of Al-Co-Ce amorphous alloys in 0.6 M NaCl solution was investigated by cyclic polarization, Mott-Schottky and X-ray photoelectron spectroscopy techniques. Results indicated that the open circuit potential of Al-Co-Ce amorphous alloys displayed a decreased tendency with the increase in Ce content, and the amorphous alloy with 4 at.% Ce presented both the lowest passive current density and donor density indicating the best corrosion resistance, while adding excess Ce led to the reduced corrosion resistance of Al-Co-Ce alloys. Furthermore, it was found that a low Ce content is beneficial to the formation of a more protective passive film on Al-Co-Ce amorphous alloys, and the corrosion inhibition reactions of Al-Co-Ce alloys in 0.6 M NaCl solution were changed with the increase in Ce content and the detailed reasons were discussed.