Characterization of spherical AlSi10Mg powder produced by double-nozzle gas atomization using different parameters

Chao-feng GAO,Zhi-yu XIAO,Hai-ping ZOU,Zhong-qiang LIU,Jin CHEN,Shang-kui LI,Da-tong ZHANG
DOI: https://doi.org/10.1016/S1003-6326(19)64947-2
IF: 3.752
2019-01-01
Transactions of Nonferrous Metals Society of China
Abstract:A self-developed double-nozzle gas atomization technique was used to produce AlSi10Mg powder. Effects of delivery tube diameter, gas pressure, and melt superheat on powder characteristics were investigated. The concepts of bluntness and outgrowth were introduced to analyze powder sphericity and satellite index quantitatively. The results showed that the median diameters of all atomized powders ranged from 25 to 33 µm. The highest yield rate (72.13%) of fine powder (<50 μm) was obtained at a superheat of 350 K. The powder size decreased with increasing melt superheat but increased with increasing delivery tube diameter. Powders with bluntness values between 96% and 98% accounted for over 60%. The outgrowth values demonstrated that 70%−85% of all powders did not contain satellite particles, with few powders adhered two or three particles. Not only Al and Si phases were present but also a metastable Al9Si phase was detected.
What problem does this paper attempt to address?