In Situ Induced Surface Reconstruction of Single-Crystal Lithium-Ion Cathode Toward Effective Interface Compatibility
Qingqing Zhang,Kai Liu,Cheng Li,Lu Li,Xingjiang Liu,Wei Li,Jinli Zhang
DOI: https://doi.org/10.1021/acsami.0c21973
2021-03-11
Abstract:LiNi<i><sub>x</sub></i>Co<i><sub>y</sub></i>Mn<sub>1–<i>x</i>–<i>y</i></sub>O<sub>2</sub> (<i>x</i> ≥ 0.5) layered oxide materials are generally considered as one of the most prospective candidates for lithium-ion battery (LIBs) cathodes due to their high specific capacity and working voltage. However, surface impurity species substantially degrade the electrochemical performance of LIBs. Herein, surface reconstruction from layered structure to disordered layer and rock-salt coherent region together with a uniform Li<sub>2</sub>CO<sub>3</sub>-dominant coating layer is first in situ constructed on the single-crystal LiNi<sub>0.5</sub>Co<sub>0.2</sub>Mn<sub>0.3</sub>O<sub>2</sub> (NCM) material by a simple water treatment procedure. The unique surface structure is elucidated by Ar-sputtering-assisted X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (spherical aberration-corrected-scanning transmission electron microscopy (STEM), high-resolution transmission electron microscopy (HRTEM), and TEM). Meanwhile, neutron powder diffraction (NPD) indicates that the antisite defect concentration is mitigated in the treated materials. The modified samples display superior cycle stability with a capacity retention of up to 87.5% at 1C after 300 cycles, a high rate capacity of 151 mAh g<sup>–1</sup> at 5C, an elevated temperature (45 °C) cycling property with 80% capacity retention (4.5 V), and improved full-cell performance with 91% after 250 cycles at 1C. Importantly, postmortem examination on the cycled cathodes by time-of-flight secondary-ion mass spectroscopy (TOF-SIMS), XPS, TEM, and X-ray diffractometer (XRD) pattern further demonstrate that these results are mainly attributed to the thin cathode electrolyte interface (CEI) film and low solubility of transition-metal ions. Therefore, this expedition provides an opportunity to construct an effective armor for the interface compatibility and stability of LIBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c21973?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c21973</a>.XRD patterns and SEM images of NCM, NCM-350 °C, NCM-400 °C, and NCM-500 °C; HRTEM and STEM image of NCM; TEM images of NCM and NCM-400 °C cathode; EDS elemental mapping of the NCM cathode particle; XPS spectra of C 1s, O 1s, and Ni 2p for NCM and NCM-400 °C with different sputtering times (0, 5, 10, 20, 30, 60, 120, 180, 240 s); XPS spectra of Li 1s for NCM and NCM-400 °C surface; cycling performance of graphite at 0.5C at 25 °C within a voltage range of 0.01–3.0 V in a half cell against lithium anodes. Digital images of lithium harvested from the disassembled cycled cells after 500 cycles at 5C for NCM and NCM-400 °C. STEM-EDX, XPS spectra in an argon atmosphere, and SEM image of cycled NCM and NCM-400 °C (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c21973/suppl_file/am0c21973_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology