Mechanism of the formation, growth and transformation of BaTi2O5 nanorods synthesized by one-step in molten-salts
Wenzhong Zou,Guoyun Zhou,Yan Hong,Wei He,Shouxu Wang,Yuanming Chen,Chong Wang,Yao Tang,Yukai Sun,Chaoying Ma
DOI: https://doi.org/10.1016/j.ceramint.2022.08.314
IF: 5.532
2023-01-01
Ceramics International
Abstract:In this work, the high-yield synthesis of BaTi2O5 (BT2) nanorods with a growth direction at [020] was achieved in the medium of KCl salt through the molten-salt synthesis (MSS) with Ba(NO3)2 and anatase TiO2 as reactants. By optimizing the involved reaction factors including particle sizes, thermal holding durations and crystalline forms of TiO2, ultra-pure BT2 nanorods with uniform size were obtained after 45 min of heating at 950 °C. Meanwhile, anatase and rutile TiO2 were respectively mixed and calcined in KCl to study the formation and transformation process of BT2 nanorods in detail. It was found that anatase TiO2 tends to merge together and convert into rutile TiO2. In particular, the formed rutile TiO2 reacts with BaO and BaTiO3 to spontaneously form BT2 nanorods without any presence of rod-like templates. Besides, BT2 takes priority over K2Ti6O13 to generate the corresponding nanorods in the molten salt with high content of K+. In addition, the O2 in air also promotes the formation of nanorods. According to the experimental results, a probable mechanism for the initial formation, subsequent growth and transformation of BT2 nanorods was thus proposed, which helps to facilitate the preparation of BT2-based one-dimensional nanomaterials.
materials science, ceramics