Abstract:Catalytic combustion has been widely applied to remove the trace combustible pollutants. However, the earth-abundant and high-performance nanocatalysts are still the main research focus on promoting catalytic efficiency. Herein, the Cu and Mn mixed oxides supported on TiO2 nanoparticles with various Cu and Mn molar contents synthesized via the flame spray pyrolysis (FSP) technique are utilized in the catalytic oxidation of lean CO and CH4. Initially, the Cu–Mn/TiO2 nanocatalysts are composed of spherical structures with a diameter of about 20 nm, whose specific surface area is between 60 and 90 m2/g. The Cu element is more evenly distributed on the TiO2 surface than the Mn element, owing to the distinctly different ion radii. Both the copper and manganese cations could incorporate into the TiO2 lattice, which generates oxygen vacancies and enhances the diffusion of oxygen ions, causing the transformation of the antanse to rutile phase. When the molar content of the Cu–Mn increases to less than 30 mol %, the temperature of its reduction peak keeps decreasing due to the hydrogen spillover effect. Moreover, the catalytic performances of the Cu–Mn/TiO2 with 12 mol % loading (12CMT) are all optimal during the low-temperature and the high-temperature stages, which are superior to the FSP-made copper manganese or copper titanium oxides. This is attributed to the small crystal particles, highly dispersed active components of CuOx and MnOx, and the higher ratios of Cu1+/Cu and Mn4+–Oads Lewis acid–base pairs. In addition, the strong interaction between Cu–Mn components and rutile phase support can tremendously promote the activity of catalytic combustion. Under the simulated flue gas, the catalytic properties of 12CMT decreases in comparison with those of CO and CH4 mixed gas due to the introduction of CO2. Ultimately, the Cu–Mn/TiO2 samples exhibit the outstanding water resistance, thanks to the hydrophobization of the catalyst surface.This article has not yet been cited by other publications.

Porous Cu-Mn-O Catalysts Fabricated by Spray Pyrolysis Method for Efficient CO Oxidation

Facile synthesis of a CuMnO<sub><i>x</i></sub> catalyst based on a mechanochemical redox process for efficient and stable CO oxidation

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

Large-scale Synthesis and Catalytic Activity of Nanoporous Cu–O System Towards CO Oxidation

In-situ fabrication of Cu-Mn-O nanostructure catalysts on Ti mesh and their catalytic property optimization for low-temperature and stable CO oxidation

Enhancing the Low-Temperature CO Oxidation over CuO-Based -MnO<sub>2</sub> Nanowire Catalysts

CuO/TiO2/Ti Monolithic Catalysts for Low-Temperature CO Oxidation

CuO/TiO 2 /Ti Monolithic Catalysts for Low-Temperature CO Oxidation

CuO Catalysts Supported on Porous TiO2 Microspheres for Low-Temperature CO Oxidation

One-Step Synthesis of Nanostructured Cu–Mn/TiO2 Via Flame Spray Pyrolysis: Application to Catalytic Combustion of CO and CH4

Revealing the intrinsic nature of Cu- and Ce-doped Mn3O4 catalysts with positive and negative effects on CO oxidation using operando DRIFTS-MS

DRIFTS-MS Investigation of Low-Temperature CO Oxidation on Cu-Doped Manganese Oxide Prepared Using Nitrate Aerosol Decomposition

Revealing the intrinsic nature of Cu- and Ce-doped Mn 3 O 4 catalysts with positive and negative effects on CO oxidation using operando DRIFTS-MS

Inverse Coprecipitation Directed Porous Core–Shell Mn–Co–O Catalyst for Efficient Low Temperature Propane Oxidation

Structure–activity Relationship of CuO/MnO2 Catalysts in CO Oxidation

Effect of the preparation method on the performance of CuO-MnO x-CeO 2 catalysts for selective oxidation of CO in H 2-rich streams

One-Step Synthesis of Nanostructured Cu–Mn/TiO 2 via Flame Spray Pyrolysis: Application to Catalytic Combustion of CO and CH 4

Copper Doped Manganese Oxides to Produce Enhanced Catalytic Performance for CO Oxidation

Enhancing CO catalytic oxidation performance over Cu-doping manganese oxide octahedral molecular sieves catalyst

Preparation and Evaluation of FeMnTi Monolithic Catalysts for High‐Efficiency CO Oxidation

Copper Manganese Oxides Supported on Multi-Walled Carbon Nanotubes As an Efficient Catalyst for Low Temperature CO Oxidation