Abstract:The spent MoSi2 modified ZrB2–SiC–MoSi2 coatings were prepared on carbon matrixes by spark plasma sintering. A continuous metallurgical bonding was formed at the interface between the coating and matrix, and no obvious defects such as pores and cracks were observed inside. The effects of spent MoSi2 content and trace doping in the spent powder on the oxidation behavior of the coatings in air at 1700 °C were investigated. During the active oxidation stage, the spent MoSi2 promoted the densification of the coating and enhanced the structural oxygen barrier properties. With the increase of service time, during the inert oxidation stage, doping an appropriate amount of spent MoSi2 helped to increase the fluidity of the rich-SiO2 protective layer so that the Zr oxides fully dispersed in the generated Zr–B–Si–O–Al multiphase glass layer, which could impede the penetration of oxygen and enhance the oxidation protection efficiency. However, excessive spent MoSi2 exacerbated the volatilization of gas by-products, forming pores and cracks in the glass layer and rising the oxidation loss. When the content of spent MoSi2 was 20 vol%, the glass layer is dense and uniform, with few defects and the best oxygen resistance property. Moreover, compared with commercial powders, spent MoSi2 contained Al2O3 and SiO2. Al2O3 had an excellent modification effect, while SiO2 glass can promote liquid phase sintering and seal the defects in the coatings. By adding spent MoSi2, the modified ZrB2–SiC–MoSi2 composite coatings could inhibit the formation of defects and improve the dynamic stability of the coatings effectively.

Preparation and Properties of ZrB2-MoSi2-glass Composite Powders for Plasma Sprayed High Temperature Oxidation Resistance Coating on C/SiC Composites

The Oxidation Behavior of ZrB2-SiC Ceramic Composites Fabricated by Plasma Spray Process

Effect of Powder Pre-Oxidation on the Microstructure and Ablation Resistance of ZrB2–SiC Coating

Oxidation ablation resistance of ZrB2-HfB2-SiC-TaSi2 coating prepared on C/C composite surface

Preparation and properties of supersonic atmospheric plasma sprayed TiB2−SiC coating

Fabrication of ZrB2-SiC powder with a eutectic phase for sintering or plasma spraying

Synthesis of In Situ ZrB2-SiC-ZrC Coating on ZrC-SiC Substrate by Reactive Plasma Spraying

Effects of SiC on microstructure and properties of plasma sprayed ZrB2–ZrC composite coating

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Static Ablation Resistance of ZrB2-SiC Composite Coatings Prepared by Atmospheric Plasma Spraying

Preparation of ZrB2-MoSi2 high oxygen resistant coating using nonequilibrium state powders by self-propagating high-temperature synthesis

MoSi2 Addition for High Ablation Resistance of Dense ZrB2-based Composite Coating Prepared by Very Low-Pressure Plasma Spraying

Optimization of Yb2O3-Gd2O3-Y2O3 Co-Doped ZrO2 Agglomerated and Calcined Powders for Air Plasma Spraying

Preparation and characterization of molybdenum disilicide coating on molybdenum substrate by air plasma spraying

Structural and Phase Transformations in Plasma-Spray ZrB2–SiC–AlN Coatings on a C/C–SiC Substrate After High-Temperature Thermal Cyclic Heating

Research Progress of the Preparation of Zirconia Hollow Sphere Powder and the Performance of Its Coating

Ablation Resistance of APS Sprayed Mullite/ZrB2-MoSi2 Coating for Carbon/Carbon Composites

Oxidation Behaviour of Plasma-Sprayed ZrB2-SiC Coatings

SPS densification and ablative performance of ZrB2–SiC–ZrC composites derived from the ternary powders by sol-gel

High-temperature oxidation resistance of spent MoSi2 modified ZrB2–SiC–MoSi2 coatings prepared by spark plasma sintering

Ablation Mechanism and Elevated Ablation Resistance of In-Situ Zrc-Zrsi2 Composite Coating Prepared by Plasma Spraying