Abstract:The size- and composition-controlled synthesis of Ni-P nanospheres from nickel chloride and sodium hypophosphite has been systematically investigated by changing the conditions, such as the ratio of the starting materials, pH value, and reduction temperature. It was found that when the starting ratio of H2PO2-/Ni2+ was changed the size and chemical composition of the nanoparticles changed simultaneously. Within a suitable pH range, the phosphorus content was altered without affecting the particle size. Increasing the reduction temperature resulted in smaller Ni-P nanospheres but invariable phosphorus content. The Ni-P nanospheres were amorphous when the phosphorus content was higher than 10.0 mol %, while lower phosphor-us content led to a composite of amorphous Ni-P and face-centered cubic (fcc) Ni. During postsynthesis calcinations, amorphous Ni-P nanospheres with a low phosphorus content directly crystallized to Ni3P and fcc Ni. However, the specimens with high phosphorus content crystallized via some intermediate phases such as Ni5P, and Ni12P5. In the latter, an amorphous P-rich shell was developed simultaneously. A preliminary catalytic test of growth of carbon nanofibers on the Ni-P nanospheres has been carried out.

Preparation and Characterization of Ni-P Ultrafine Catalyst Particles with Narrow Size Distribution

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

A STUDY ON THE PREPARATION AND PROPERTIES OF AMORPHOUS NI-P ULTRAFINE PARTICLES

Synthesis and characterization of NiP–TiO2 ultrafine composite particles

Spherical amorphous nickel-phosphorus alloy particles with uniform size prepared at room temperature

Controllable preparation of Ni nanoparticles for catalysis of coiled carbon fibers growth.

Noble Metal Catalyzed Preparation of Ni2P/α-Al2O3

Preparation and Characterization of Bulk and Supported NiB Amorphous Alloy Catalysts with Different Particle Sizes

Experimental Study on Synthesis of Nio Nano-Particles

Controlled synthesis, characterization, and crystallization of Ni-P nanospheres.

A STUDY ON THE REACTION-KINETICS FOR THE PREPARATION OF NI-P ULTRAFINE AMORPHOUS ALLOY BY AN INDUCED AUTOCATALYTIC METHOD

Ultrafine Amorphous Fe-Ni-B And Fe-P-B Particles

Preparations,Structures and Properties of Amorphous Ni-P Alloy Catalysts

Preparation and Characterization of Ni Nanopowders Prepared by Anodic Arc Plasma

Preparation and Characterization of Monodisperse FePd Nanoparticles

Low-Temperature Solution-Phase Synthesis of NiAu Alloy Nanoparticles Via Butyllithium Reduction: Influences of Synthesis Details and Application As the Precursor to Active Au-NiO/SiO2 Catalysts Through Proper Pretreatment

Preparation of Ni-P Amorphous Alloy Ultrafine Powders

Preparation of ultrafine powders of Ni(OH)2 and NiO by coordination-precipitate method

Preparation and Characterization of Mono-disperse Spherical Nickel Particles

Amorphous Ni-B hollow spheres synthesized by controlled organization of Ni-B nanoparticles over PS beads via surface seeding/electroless plating