Interactions Between Fe-rich Intermetallics and Mg-Si Phase in Al-7Si-xMg Alloys

Xiaoyan Wu,Huarui Zhang,Zhen Ma,Tongxiang Tao,Jing Gui,Wei Song,Bo Yang,Hu Zhang

DOI: https://doi.org/10.1016/j.jallcom.2019.01.352

IF: 6.2

2019-01-01

Journal of Alloys and Compounds

Abstract:This paper investigated the influences of Mg level (0.3 wt%-0.6 wt%) and heat treatment process on the phase transformation of Mg-Si phase and Fe-rich intermetallics of low pressure die-cast Al-7Si-xMg alloys. Their corresponding mechanical properties were also studied. The results indicated that at as-cast state, the addition of Mg element accelerated the formation of pi-Fe phase while the mechanical properties decreased correspondingly. During the heat treatment process, the transformation of Mg-Si phase and pi-Fe intermetallics were determined by the Mg content. In the alloys with low level of 0.3 wt% -0.45 wt% Mg, the diffusion of Mg element from pi-Fe phase into alpha-Al matrix prompted the formation of more Mg2Si strengthening phase, which was beneficial to the improvement of tensile properties. However, in the alloys with high level of 0.6 wt% Mg, the diffusion kinetic of Mg element from pi-Fe phase into alpha-Al matrix was repressed due to the saturated Mg in the matrix. The pi-Fe phase consumed large amount of Mg element and facilitated crack initiation which definitely weakened the strengthening effect. The mechanical properties, especially the ductility, were strongly deteriorated. In this study, the best comprehensive mechanical properties were obtained from the Al-75i-0.45 Mg alloy, which was 267.3 MPa and 333.7 MPa, 9% for YS, UTS and Elongation, respectively. (C) 2019 Elsevier B.V. All rights reserved.