Effects of Mg on the Microstructure and Mechanical Property of Al-Si-Mg Casting Alloys

陈忠伟,介万奇

DOI: https://doi.org/10.3969/j.issn.1673-2812.2004.05.007

2004-01-01

Abstract:The microstructures and mechanical properties of three Al-7wt%Si-Mg casting alloys, with Mg contents of 0.00wt% , 0.35wt% and 0.70wt%, have been studied. Various microstructures were produced by changing the solidification rate and by modification with Al-10Sr modifier. DSC tests were carried out to determine the phases in various Mg contents alloys. The eutectic Si phase in the unmo- dified alloys and in the Sr-modified alloys become larger in the alloys with higher Mg content. Large Fe-rich π-phases (Al 9FeMg 3Si 5) are found in the 0.70wt% Mg alloys together with some smaller β-phases (Al 5FeSi); in contrast, only β-phases are observed in the 0.35wt% Mg alloys. The tensile strength increases with the Mg content. The tensile ductility is less than in the higher Mg alloys, especially in the Sr-modified alloys, compared with the lower Mg alloys.