Abstract:The diffusion bonding of YG8 cemented carbide and 40Cr steel was performed using spark plasma sintering with Ni powder as the interlayer. The influence of bonding temperatures ranging from 700 to 1100 degrees C on the bonding interface morphology, mechanical properties, and failure mechanism of the joints was studied. By calculating the diffusion coefficients of Ni and Fe and observing the changes in the interface morphology, the pores at the Ni/ 40Cr interfaces were identified as Kirkendall voids formed because of the unbalanced diffusion of Ni and Fe. The diffusion activation energy of Ni in Fe was 87.37 kJ/mol, and that of Fe in Ni was 58.08 kJ/mol. The use of a pulsed current significantly reduced the diffusion activation energy, making diffusion easier. The bending strength of the joints increased sharply in the range from 700 to 900 degrees C, subsequently increased slowly, and tended to stabilise in the range from 900 to 1100 degrees C. The highest bending strength of 1080 MPa was achieved for the joint bonded at 1100 degrees C, which was attributed to the improved bonding of the YG8/Ni and Ni/40Cr interfaces and the resulting effects of the interlayer plastic constraint. The thickness of the Co-Ni diffusion zone at the YG8/Ni interface appeared to form a decisive factor in determining the failure locations of the joints. As the bonding temperature increased, the improved diffusion of Co and Ni enhanced the metallurgical bonding of the YG8/Ni interface, and the fracture position shifted from the polished surface of the YG8 base material (700 degrees C) to the Ni interlayer (1100 degrees C).

Effects of Boron and Silicon on Microstructural Evolution and Mechanical Properties of Transient Liquid Phase Bonded GH3039/IC10 Joints

Transient Liquid Phase Bonding of IC10 Single Crystal with GH3039 Superalloy Using BNi2 Interlayer: Microstructure and Mechanical Properties

Diffusion Brazing of GH536 Polycrystalline Superalloy with IC10 Single Crystal Superalloy Using BNi-2 Interlayer

Effect of Bonding Pressure on Transient Liquid Phase Bonding Joint Microstructure and Properties of T91/12Cr2MoWVTiB

Effects of Bonding Temperature on Mechanical Properties and Interfacial Morphology of YG8/40Cr Joints Fabricated Using SPS Diffusion Bonding

Microstructure and Mechanical Property of GH4169 Joints by Vacuum Diffusion Bonding

The Effects of Borides on the Mechanical Properties of Tlpb Repaired Inconel 738 Superalloy

Microstructure and Mechanical Properties of Ti-48Al-2Cr-2Nb Alloy Joints Produced by Transient Liquid Phase Bonding Using Spark Plasma Sintering

Experimental and Numerical Study of Transient Liquid Phase Diffusion Bonded DZ40M Superalloys

Effect of GNPs on Interfacial Microstructure Evolution and Mechanical Property of Cf/SiC-GH99 Joints

Microstructure and properties of GH4169 vacuum diffusion bonded joint

Effect of holding time on microstructure and mechanical properties of dissimilar γ'‐strengthened superalloys TLP joint

Microstructure and Mechanical Properties of Vacuum Diffusion Bonding Joints for Γ-Tial Based Alloy

Evolution of microstructure and mechanical properties on dissimilar transient liquid phase (TLP) bonding of GTD-111 and IN-718 by BNi-9 (AWS A5.8/A5.8M) interlayer

Effect of bonding parameters on microstructures and properties during TLP bonding of Ni-based super alloy

Effect of Post-Bond Heat Treatment on the Microstructure and High Temperature Mechanical Property of a TLP Bonded Γ′-Strengthened Co-Based Single Crystal Superalloy

Quasi-in-situ Observation of Interfacial Behaviours:Recrystallization and Grain Recombination During Micro-deformed Diffusion Bonding Process

Microstructure Evolution at the Diffusion Bonding Interface of High Nb Containing TiAl Alloy

A Novel Composite Interlayer Assembled for C/SiC-GH99 Brazed Joints

Microstructure and Mechanical Properties of Cf/SiC Composite/gh99 Joints Brazed with BNi2-Ti Composite Filler

Effects of the joining process on the microstructure and properties of liquid-phase-sintered SiC-SiC joints formed with Ti foil