Abstract:The Cu materials are playing an irreplaceable role in modern marine facilities, while one major issue affecting their service life is corrosion attack caused by external erosion of chloride ions, which leads to the quickly structural deterioration and reduced durability. To solve this obstinate issue, the corrosion−resistant Ni−based composite films with conductive Yttria–stabilized zirconia (YSZ, 2.5–15 g/L) and non−conductive Si 3 N 4 (2.5–15 g/L) reinforcing phases were composite–electrodeposited on Cu substrate in direct current (DC) mode. It was believed that the electrical differences of incorporated nanoparticles have a significant impact on nucleation and growth behaviors during electrodeposition, which further altered the structure and property of Ni−based composite films. Therefore, the emphasis of this study was to establish the correlation between obtained structure, electrochemical, and immersion corrosion performances at different incorporation levels of YSZ/Si 3 N 4 nanoparticles. The results demonstrate that by increasing the total doping contents, the Electrochemical Impedance Spectroscopy (EIS) and Chronoamperometry (CA) measurements exhibited an initial increase followed by a subsequent decrease on co−deposition dynamics, which was related to the dominant impact of conductive YSZ nanoparticle at electrocrystallization process. Meanwhile, the moderate incorporation level of 15 g/L offered effective control over structural compactness through dispersion−strengthening and grain−refining, and the same ratio of YSZ/Si 3 N 4 nanoparticles further maximized the improvement degree of microhardness, electrochemical passivation, and immersion stability of resulting films. Besides, the corrosion current density ( j corr ) of Ni−YSZ−Si 3 N 4 composite coating under optimum condition of 15 g/L was two orders of magnitude smaller than that of Cu substrate after long−term immersion test, and the corresponding polarization resistance ( R p ) also increased by 8.6 times. Overall, these substantial alterations obtained provide effective guideline for the design and preparation of corrosion−resistant Ni−based composite coating, which is beneficial to prolonging the service life of Cu components in saline environments.

Study on Erosion-Corrosion Mechanism of B10 Cu-Ni Alloy in Seawater

The Effect of Ni201 Transition Layer on the Corrosion, Wear and Synergetic Cavitation Erosion-Corrosion Behavior of CMT-Monel K500 Coating

Influence of Ni Addition on Corrosion Performance of Medium-temperature Filler Metal with Low Cu Content for Al Brazed Joints

Long-Term Corrosion Behavior of Cu-10Ni and Cu-20Ni Alloys in Simulated Seawater

Insight to corrosion mechanism of 90/10 copper-nickel alloys under different sea depths

Multiscale characterization of seawater pipe erosion of B10 copper-nickel alloy welded joints

Corrosion of Copper-Nickel Alloys in Seawater-Based Electrolytes

Erosion-corrosion behavior of Nickel based alloys in supercritical water oxidation environment

Erosion-corrosion behavior of Ni-Al-Cu coating on nickel-aluminium bronze alloy in 3.5 wt.% NaCl solution

Corrosion behavior of B10 copper-nickel alloy beneath a deposit caused by sulfate-reducing bacteria with carbon source starvation in marine environments

Why does seawater corrosion significantly inhibit the cavitation erosion damage of nickel-aluminum bronze?

Electrochemical Corrosion Behavior of Cu-15Ni-8Sn Alloy in Marine Microbial Medium

A Ni-Cu/CuPP composite coating with good wear resistance and long-term corrosion resistance for seawater applications

Study on the Effects of Fluid Parameters on Erosion-Enhanced Corrosion of 90/10 Copper–Nickel Alloy Using Wire Beam Electrode

Antagonistic effect of electrochemical corrosion on the mechanical wear of Monel 400 alloy in seawater

An Experimental Study on Cavitation Erosion-Corrosion Performance of ANSI 1020 and ANSI 4135 Steel

Erosion-corrosion behaviour of shot peening treated nickel-aluminium bronze in simulated sand-containing seawater

Electrodeposition fabrication of corrosion−resistant Ni–based composite film on surface of Cu: Role of conductive YSZ and non−conductive Si 3 N 4 nanoparticles

Clarifying the effect of Cu element on the corrosion properties of Ni-Mo low alloy steel in marine environment

Effect of seawater salinity on the fretting corrosion behavior of nickel-aluminum bronze (NAB) alloy

The erosion-corrosion behaviors of the full-scale Ni-P and Ni-Cu-NiW internal coating tubing