Abstract:TixCr1 - yFeyMn1.0 (x = 1.02, 1.05, 1.1, 0.05 <= y <= 0.25) alloys were prepared by plasma arc melting and annealing at 1273 K for 2 hours. The XRD results show that the main phase of all alloys is the C14 type Laves phase, and a little secondary phase exists in a mixture of the binary alloy phase. The lattice parameters increase with Ti super-stoichiometry ratio increasing, whereas smaller lattice parameters emerge with increasing Fe stoichiometry content. Additionally, as the Ti super-stoichiometry ratio decreases, the pressure-composition-temperature measurements indicated that hydrogen absorption and desorption plateau pressures of TixCr0.9Fe0.1Mn1.0 (x = 1.1, 1.05, 1.02) alloys increase from 3.15, 0.67, to 5.94, 1.13 MPa at 233 K, respectively. On the other hand, with the Fe content increasing in Ti1.05Cr1 - yFeyMn1.0 (0.1 <= y <= 0.25) alloys from 0.1 to 0.25, the hydrogen desorption plateau pressures increased from 1.41 to 2.46 MPa at 243 K. The hydrogen desorption plateau slopes reduce to 0.2 with Ti super-stoichiometry ratio decreasing to 1.02, but the alloys are very difficult to activate for hydrogen absorption and cannot activate when the Fe substituting for Cr exceeds 0.2. The maximum hydrogen storage capacities were more than 1.85 wt% at 201 K. The reversible hydrogen storage capacities can remain more than 1.55 wt% at 271 K. The enthalpy and entropy for all hydride dehydrogenation are in the range of 21.0 to 25.5 kJ/mol H-2 and 116 to 122 J mol(-1) K-1, respectively. Our results suggest that Ti1.05Cr0.75Fe0.25Mn1.0 alloy with low enthalpy holds great promise for a high hydrogen pressure hybrid tank in a hydrogen refueling station (45 MPa at 333 K), and the other alloys of low cost may be used for a potable hybrid tank due to high dissociation pressure at 243 K and high volumetric density exceeding 40 kg/m(3).

Model for Hydrogen Desorption Plateau Pressure of AB2 Type-Tix(crfemn)2 Alloys

Experimental and Theoretical Investigation on the Enhanced Hydrogen Storage Performance of Ti–Cr–Mn–Fe-Based Alloys Modified by Nb Substitution

Effect of Rare Earth Doping on the Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application

Development of Ti–Zr–Mn–Cr-(V–Fe) Based Alloys for Hydrogen Feeding System in Hydrogen Metallurgy Application

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Stability of AB5-type hydrogen storage alloys

Development of Ti–Cr–Mn–Fe Based Alloys with High Hydrogen Desorption Pressures for Hybrid Hydrogen Storage Vessel Application

Influence of Fe Content on the Microstructure and Hydrogen Storage Properties of Ti16Zr5Cr22V57−xFex (x = 2–8) Alloys

Hydrogen storage properties of TiMn2-based alloys

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

The Effect of Cr Content on the Structural and Hydrogen Storage Characteristics of Ti10V80−xFe6Zr4Crx (x = 0–14) Alloys

Phase Structure and Hydrogen Storage Properties of Ti17cr23v55-Xzr5fex (X=11 Similar to 16) Alloys

Influence of element substitution on structural stability and hydrogen storage performance: A theoretical and experimental study on TiCr2-xMnx alloy

Development of Ti1.02Cr2-x-yFexMny (0.6≤x≤0.75, Y=0.25, 0.3) Alloys for High Hydrogen Pressure Metal Hydride System

Influence of Ti Super-Stoichiometry on the Hydrogen Storage Properties of Ti1+xCr1.2Mn0.2Fe0.6 (x = 0–0.1) Alloys for Hybrid Hydrogen Storage Application

Effect of Mn substitution on plateau pressure regulation of the Ti0.92Zr0.1Cr1.6−xMnxFe0.4 alloys for primary hydrogen compressor

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

High-Pressure Hydrogen Storage Properties Of Tixcr1-Yfeymn1.0 Alloys

Phase Structures and Hydrogen Storage Properties of TiV1.35Cr1.35-xMnx Alloys(x=0～0.45)

Low-cost Vanadium-Free Ti–Zr–Cr–Mn–Fe Based Alloys for Metal Hydride Hydrogen Compressor under Mild Conditions

Improving the plateau performance of the TiZrFeMnCrV high-entropy alloy by partial substitution of V with fe, Mn and cr