Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

High Temperature Tensile Behavior of a Thin-Walled Ni Based Single-Crystal Superalloy with Cooling Hole: In-situ Experiment and Finite Element Calculation

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Tensile behavior of single-crystal superalloy with different structured cooling holes

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

In-Situ Study of High Temperature Tensile Fracture Mechanism of Mar-M247 Alloy

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Quantitative Study of High-Frequency Fatigue Hole-Edge Stresses in Nickel-Based Single-Crystal Superalloy

Orientation and temperature dependence of yielding and deformation behavior of a nickel-base single crystal superalloy

Investigation of in Situ 1150 Degrees C High Temperature Deformation Behavior and Fracture Mechanism of a Second Generation Single Crystal Superalloy

The Dependence of Stress and Strain Rate on the Deformation Behavior of a Ni‐based Single Crystal Superalloy at 1050°C

Creep rupture mechanism and microstructure evolution around film-cooling holes in nickel-based single crystal superalloy specimen

Microstructure and Elevated Temperature Tensile Behaviour of Directionally Solidified Nickel Based Superalloy

Tensile Deformation Behavior of Typical Porous Laminate Structure at Different Temperatures

Temperature effects on tensile behaviors and relevant deformation mechanisms of a low-cost nickel-based single crystal superalloy containing 1.5% Re

A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy

Effect of Temperature on the Tensile Deformation Mechanisms of a Fourth Nickel-Based Single Crystal Superalloys

Temperature Dependence of High-Cycle Fatigue Behavior of a Ni-Base Single Crystal Superalloy

Effect of μ precipitation and γ′ evolution on intra/intergranular strength of Ni-Co-Cr-based superalloys after 800 °C thermal exposure

Multiscale analysis of interior cracking behavior of Ni-based superalloy fabricated by selective laser melting under very-high-cycle-fatigue at high-temperature

Temperature dependence of deformation behavior, microstructure evolution and fracture mechanism of Inconel 625 superalloy