Abstract:In order to study the combined action of compression-bending load and surrounding ion erosive environment on underwater shield tunnel, a series of cofferdam-type electrochemical-accelerated corrosion tests of mini segments are carried out to investigate the segment reinforcement corrosion under different compression-bending loads and the change of internal force and rigidity of mini segments under different load-bearing and corroding conditions. Then, the failure pattern of mini segments under different loading and corroding states are recorded and analyzed. The results indicate that the following: (1) the larger the external load, the shorter the initial rust time of the steel bar; (2) the corrosion rate of steel bar increases linearly with time, and the ratio of corrosion of steel bar increases quadratically with time, the larger the load, the more obvious the increase will be; (3) after the corrosion of steel bar, the change rate of the strain for the steel bar increases as the external load augments, and as a matter of fact, the change rate of the strain increases as well, besides, the degree of strain change for compressive steel is obviously lower compared with that of tensile steel bar; (4) the effect of electric corrosion on the deflection of the segments is more obvious with the increase of external load, and a quadratic increase relationship between the deflection and the corrosion is observed in the process of corrosion; (5) It can be concluded that plastic failure is observed for the segments without loading and for those without cracks in the initial stage of loading, which can be indicated directly by the relatively smaller loss rate of steel section, while brittle failure is presented as the failure pattern for the segments with cracks after loading for certain period, which means the loss rate of steel section is relatively larger. The results can briefly provide useful reference for rational design and durability assessment of shield tunnel segmental linings.

The Degradation of Macro-Mechanical Properties of Shield Tunnel Segments

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Mechanical‐performance deterioration of RC segment of shield tunnel under high corrosion degree and the transformation of eccentric‐failure mode

Mechanical Degradation of Reinforced Concrete Columns Corroded Under Sustained Loads

Study on Degradation Regularity of Bearing Capacity of RC Beams under Corrosive Conditions

Experiment study on chloride corrosion deterioration of load-bearing concrete segment

Effects of Reinforcement Corrosion and Sustained Load on Mechanical Behavior of Reinforced Concrete Columns.

Full-Scale Experimental Study on the Effect of Ground Surcharge on the Stress and Deformation of Shield Tunnels

Full-scale Loading Test for Shield Tunnel Segments: Load-bearing Performance and Failure Patterns of Lining Structures

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Full-scale Experimental and Structural Characterization Study of Shield Tunnel Reinforcement under Ground Stacking Loads

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Crack Propagation and Flexural Behaviour of Rc Beams under Simultaneous Sustained Loading and Steel Corrosion

Compressive Behaviour of Corroded Thin-Walled Circular Section Steel Stub Columns

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Experimental study on bearing capacity and ductility of reinforced concrete beam in multi-aggressive and loading coupling

Full-scale testing and numerical modelling of segmental-joint performance with corroded bolt

Experimental study on the high water pressure erosion mechanism and its influence on the submarine shield tunnel concrete segments

Degradation mechanism and life prediction of cemented tailings backfill under dry–wet cycles and salt erosion

Mechanical performances of shield tunnel segments under asymmetric unloading induced by pit excavation

Shaking Table Tests of Coastal Bridge Piers with Different Levels of Corrosion Damage Caused by Chloride Penetration